Effect of Relative Humidity on the Initial Atmospheric Corrosion Behavior of Zinc during Drying | |
Cheng, Qingli1,2; Song, Shanhua1,2; Song, Liying1,2; Hou, Baorong1 | |
刊名 | JOURNAL OF THE ELECTROCHEMICAL SOCIETY |
2013 | |
卷号 | 160期号:8页码:C380-C389 |
ISSN号 | 0013-4651 |
通讯作者 | Cheng, QL |
中文摘要 | The effects of relative humidity on the initial atmospheric corrosion of zinc during drying of chloride-contained absorbed thin electrolyte layer was investigated by mass loss, scanning electron microscopy (SEM), cathodic polarization curves, pre-Tafel polarization curves fitting method and electrochemical impedance spectroscopy (EIS). The results showed that the zinc corrosion rate decreased with increasing relative humidity in the first 2 h. After 72 h of exposure, the corrosion rates of zinc were ranked as: 75% RH < 85% RH < 97% RH. And the morphology of corrosion products at 75% RH appeared more compact than that of 85% and 97% RH. (C) 2013 The Electrochemical Society. All rights reserved. |
英文摘要 | The effects of relative humidity on the initial atmospheric corrosion of zinc during drying of chloride-contained absorbed thin electrolyte layer was investigated by mass loss, scanning electron microscopy (SEM), cathodic polarization curves, pre-Tafel polarization curves fitting method and electrochemical impedance spectroscopy (EIS). The results showed that the zinc corrosion rate decreased with increasing relative humidity in the first 2 h. After 72 h of exposure, the corrosion rates of zinc were ranked as: 75% RH < 85% RH < 97% RH. And the morphology of corrosion products at 75% RH appeared more compact than that of 85% and 97% RH. (C) 2013 The Electrochemical Society. All rights reserved. |
学科主题 | Electrochemistry ; Materials Science |
WOS标题词 | Science & Technology ; Physical Sciences ; Technology |
类目[WOS] | Electrochemistry ; Materials Science, Coatings & Films |
研究领域[WOS] | Electrochemistry ; Materials Science |
关键词[WOS] | THIN ELECTROLYTE LAYERS ; ELECTROCHEMICAL IMPEDANCE SPECTROSCOPY ; AERATED SULFATE MEDIUM ; AC-IMPEDANCE ; PITTING CORROSION ; IN-SITU ; POLARIZATION CURVES ; OXYGEN REDUCTION ; STAINLESS-STEEL ; DISSOLUTION |
收录类别 | SCI |
原文出处 | 10.1149/2.078308jes |
语种 | 英语 |
WOS记录号 | WOS:000324810000064 |
公开日期 | 2014-07-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.qdio.ac.cn/handle/337002/16362] |
专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
作者单位 | 1.Chinese Acad Sci, Inst Oceanol, Natl Engn Res Ctr Marine Corros Protect, Qingdao 266071, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Cheng, Qingli,Song, Shanhua,Song, Liying,et al. Effect of Relative Humidity on the Initial Atmospheric Corrosion Behavior of Zinc during Drying[J]. JOURNAL OF THE ELECTROCHEMICAL SOCIETY,2013,160(8):C380-C389. |
APA | Cheng, Qingli,Song, Shanhua,Song, Liying,&Hou, Baorong.(2013).Effect of Relative Humidity on the Initial Atmospheric Corrosion Behavior of Zinc during Drying.JOURNAL OF THE ELECTROCHEMICAL SOCIETY,160(8),C380-C389. |
MLA | Cheng, Qingli,et al."Effect of Relative Humidity on the Initial Atmospheric Corrosion Behavior of Zinc during Drying".JOURNAL OF THE ELECTROCHEMICAL SOCIETY 160.8(2013):C380-C389. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论