Solvothermal synthesis of CeF3: Er3+, Yb3+ nanoplates with visible upconversion luminescence by 980 nm excitation | |
Sheng TQ ; Fu ZL ; Han YY ; Zhang SY ; Dai ZW | |
刊名 | materials research bulletin |
2013 | |
卷号 | 48期号:2页码:884-888 |
关键词 | WAVE-GUIDE LASER 3-DIMENSIONAL DISPLAY FIBER LASER GLASS PHOSPHORS |
ISSN号 | 0025-5408 |
通讯作者 | fu zl |
中文摘要 | cef3: er3+, yb3+ nanoplates have been successfully synthesized by a solvothermal method with further calcinations. the crystalline phase, size and optical properties were characterized using powder x-ray diffraction (xrd), field emission-scanning electron microscopy (fe-sem), x-ray photoelectron spectroscopy (xps), energy dispersive spectroscopy.(eds) and upconversion luminescence (ucl). all the as-prepared samples showed blue emission (487 nm), green emissions (523 nm, 546 nm) and red emission (654 urn) under 980 nm excitation. the main mechanism of upconversion is attributed to the energy transfer (et) among yb3+ and er3+ ions in excited states. the results illustrate the large potential of this new class of material for photonic applications involving optoelectronics devices. (c) 2012 elsevier ltd. all rights reserved. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000315751300112 |
公开日期 | 2014-04-16 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/50058] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Sheng TQ,Fu ZL,Han YY,et al. Solvothermal synthesis of CeF3: Er3+, Yb3+ nanoplates with visible upconversion luminescence by 980 nm excitation[J]. materials research bulletin,2013,48(2):884-888. |
APA | Sheng TQ,Fu ZL,Han YY,Zhang SY,&Dai ZW.(2013).Solvothermal synthesis of CeF3: Er3+, Yb3+ nanoplates with visible upconversion luminescence by 980 nm excitation.materials research bulletin,48(2),884-888. |
MLA | Sheng TQ,et al."Solvothermal synthesis of CeF3: Er3+, Yb3+ nanoplates with visible upconversion luminescence by 980 nm excitation".materials research bulletin 48.2(2013):884-888. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论