Synthesis and Luminescent Properties of GdNbO4:RE3+ (RE = Tm, Dy) Nanocrystalline Phosphors via the Sol-Gel Process | |
Lu Y ; Tang XH ; Yan LS ; Li KX ; Liu XM ; Shang MM ; Li CX ; Lin J | |
刊名 | journal of physical chemistry c
![]() |
2013 | |
卷号 | 117期号:42页码:21972-21980 |
关键词 | FIELD-EMISSION DISPLAYS LIGHT-EMITTING-DIODES HOST-SENSITIZED LUMINESCENCE RARE-EARTH PHOTOLUMINESCENCE PROPERTIES ENERGY-TRANSFER BLUE TB3+ EXCITATION EFFICIENT |
ISSN号 | 1932-7447 |
通讯作者 | liu xm |
中文摘要 | nanocrystalline gdnbo4:tm3+ and gdnbo4:dy3+ phosphors were prepared through a pechini-type sol gel process. x-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, photoluminescence, and cathodoluminescence (cl) spectra were utilized to characterize the synthesized phosphors. xrd reveals that the samples begin to crystallize at 900 degrees c and the pure gdnbo4 phase can be obtained at 1000 degrees c. fe-sem images indicate that the gdnbo4:tm3+ and gdnbo4:dy3+ samples consist of fine and spherical grains with a size around 30-50 nm. under the excitation of uv light (264 nm) and low-voltage electron beams (1-3 kv), the gdnbo4:tm3+ and gdnbo4:dy3+ phosphors showed the characteristic emissions of tm3+ (d-1(2) -> h-3(6), h-3(5), h-3(4), and (1)g(4) -> h-3(6) transitions) and dy3+ (f-4(9/2) -> h-6(15/2) and f-4(9/2) -> h-6(13/2) transitions), respectively. the blue cl of the gdnbo4:tm3+ phosphor has higher color purity and comparable intensity to the y2sio5:ce3+ commercial product. a single-composition white light emitting in response to near uv and low-voltage electron beam excitation has been realized in gdnbo4:dy3+ phosphor. the obtained gdnbo4:tm3+ and gdnbo4:dy3+ phosphors have potential applications in the areas of near uv white-light-emitting diodes and field emission display devices. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000326260000043 |
公开日期 | 2014-04-15 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/49529] ![]() |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Lu Y,Tang XH,Yan LS,et al. Synthesis and Luminescent Properties of GdNbO4:RE3+ (RE = Tm, Dy) Nanocrystalline Phosphors via the Sol-Gel Process[J]. journal of physical chemistry c,2013,117(42):21972-21980. |
APA | Lu Y.,Tang XH.,Yan LS.,Li KX.,Liu XM.,...&Lin J.(2013).Synthesis and Luminescent Properties of GdNbO4:RE3+ (RE = Tm, Dy) Nanocrystalline Phosphors via the Sol-Gel Process.journal of physical chemistry c,117(42),21972-21980. |
MLA | Lu Y,et al."Synthesis and Luminescent Properties of GdNbO4:RE3+ (RE = Tm, Dy) Nanocrystalline Phosphors via the Sol-Gel Process".journal of physical chemistry c 117.42(2013):21972-21980. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论