The mechanical properties of an aluminum alloy by plasma-based ion implantation and solution-aging treatment | |
Zhan, ZJ ; Ma, XX ; Sun, Y ; Xia, LF ; Liu, QY | |
刊名 | SURFACE & COATINGS TECHNOLOGY |
2000 | |
卷号 | 128页码:256 |
关键词 | WEAR BEHAVIOR NITROGEN |
ISSN号 | 0257-8972 |
通讯作者 | Zhan, ZJ (reprint author), Chinese Acad Sci, Inst Phys, POB 603, Beijing 100080, Peoples R China. |
中文摘要 | The age-strengthening 2024 aluminum alloy was modified by a combination of plasma-based ion implantation (PBII) and solution-aging treatments. The depth profiles of the implanted layer were investigated by X-ray photoelectron spectroscopy (XPS). The structure was studied by glancing angle X-ray diffraction (GXRD). The variation of microhardness with the indenting depth was measured by a nanoindenter. The wear test was carried on with a pin-on-disk wear tester. The results revealed that when the aluminum alloys were implanted with nitrogen at the solution temperature, then quenched in the vacuum chamber followed by an artificial aging treatment for an appropriate time, the amount of AIN precipitates by the combined treatment were more than that of the specimen implanted at ambient temperature. Optimum surface mechanical properties were obtained. The surface hardness was increased and the weight loss in a wear test decreased too. (C) 2000 Published by Elsevier Science S.A. All rights reserved. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-23 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/45321] |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Zhan, ZJ,Ma, XX,Sun, Y,et al. The mechanical properties of an aluminum alloy by plasma-based ion implantation and solution-aging treatment[J]. SURFACE & COATINGS TECHNOLOGY,2000,128:256. |
APA | Zhan, ZJ,Ma, XX,Sun, Y,Xia, LF,&Liu, QY.(2000).The mechanical properties of an aluminum alloy by plasma-based ion implantation and solution-aging treatment.SURFACE & COATINGS TECHNOLOGY,128,256. |
MLA | Zhan, ZJ,et al."The mechanical properties of an aluminum alloy by plasma-based ion implantation and solution-aging treatment".SURFACE & COATINGS TECHNOLOGY 128(2000):256. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论