Formation of 1:13 Phase in La(Fe,Si)(13)-Based Compounds by Diffusion of LaFe,Si/alpha-Fe(Si) Couple | |
Fu, S ; Long, Y ; Wang, CL ; Zhang, M ; Soumei, O ; Hu, FX | |
刊名 | IEEE TRANSACTIONS ON MAGNETICS |
2012 | |
卷号 | 48期号:11页码:3757 |
ISSN号 | 0018-9464 |
通讯作者 | Long, Y: Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China. |
中文摘要 | Formation mechanism of the 1:13 phase in La(Fe,Si)(13) compounds has been investigated by the diffusion of LaFeSi/alpha - Fe(Si) couple at 1353 K and 1443 K. After annealing at 1353 K for 12 days, 0.8 mm thick 1:13 phase was obtained between LaFeSi and alpha - Fe(Si) sheets. A layer of La5Si3 phase determined by EDS appeared all along the interface of LaFeSi and 1:13 phase. In addition, La5Si3 phase was also found in grain boundary of 1:13 phase grains and La-rich phase was found in grain boundary of alpha - Fe(Si) sheet. It is believed that La5Si3 phase and grain boundaries working as rapid diffusion paths were important for the formation of 1:13 phase in La(Fe,Si)(13) compounds. 1:13 phase mainly formed in the alpha - Fe(Si) master alloy sheet. In addition, large grains of 1:13 phase were close to the LaFeSi sheet and small grains of 1:13 phase were close to alpha - Fe(Si) layer. It indicated that La and Si elements diffused from LaFeSi sheet to alpha - Fe(Si) sheet in the formation process of 1:13 phase. There was an endothermic peak at 207 K in the DSC curve of the 1:13 phase obtained from diffusion couple annealed at 1353K. It indicated the occurrence of magnetic phase transition. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2013-09-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.iphy.ac.cn/handle/311004/38378] |
专题 | 物理研究所_物理所公开发表论文_物理所公开发表论文_期刊论文 |
推荐引用方式 GB/T 7714 | Fu, S,Long, Y,Wang, CL,et al. Formation of 1:13 Phase in La(Fe,Si)(13)-Based Compounds by Diffusion of LaFe,Si/alpha-Fe(Si) Couple[J]. IEEE TRANSACTIONS ON MAGNETICS,2012,48(11):3757. |
APA | Fu, S,Long, Y,Wang, CL,Zhang, M,Soumei, O,&Hu, FX.(2012).Formation of 1:13 Phase in La(Fe,Si)(13)-Based Compounds by Diffusion of LaFe,Si/alpha-Fe(Si) Couple.IEEE TRANSACTIONS ON MAGNETICS,48(11),3757. |
MLA | Fu, S,et al."Formation of 1:13 Phase in La(Fe,Si)(13)-Based Compounds by Diffusion of LaFe,Si/alpha-Fe(Si) Couple".IEEE TRANSACTIONS ON MAGNETICS 48.11(2012):3757. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论