The Solubility and Temperature Dependence of Resistivity for Aluminum-Doped Zinc Oxide Ceramic

CORC > 宁波材料技术与工程研究所 > 中国科学院宁波材料技术与工程研究所 > 宁波所知识产出

	The Solubility and Temperature Dependence of Resistivity for Aluminum-Doped Zinc Oxide Ceramic
	Song WJ(宋伟杰) ; Yulong Zhang, Weiyan Wang
刊名	Int. J. Appl. Ceram. Technol.
	2012-06-29
期号	2 页码:374—381
通讯作者	宋伟杰
合作状况	李雨桐
中文摘要	The solubility of Aluminum (Al)-doped ZnO ceramic was determined to be 0.9 atomic ratio percent (at.%), and the ZnAl2O4 was formed once the Al content achieved 1.0 at.% or above. The resistivity decreased at an Al content of 0–0.8 at.% to a minimum of 1.45 10 3 O, while increased at a range of 1.0–6.0 at.%. The resistivity increased and decreased with temperature when the Al content was below and above 2.0 at.%, respectively. The activation energy increased from 489.5 to 65.0 eV and from 66.0 to 293.8 eV when the Al doping content was below and above 2.0 at.%.
学科主题	物理化学
原文出处	SCI收录
公开日期	2013-12-16
内容类型	期刊论文
源URL	[http://ir.nimte.ac.cn/handle/174433/9649]
专题	宁波材料技术与工程研究所_宁波所知识产出
推荐引用方式 GB/T 7714	Song WJ,Yulong Zhang, Weiyan Wang. The Solubility and Temperature Dependence of Resistivity for Aluminum-Doped Zinc Oxide Ceramic[J]. Int. J. Appl. Ceram. Technol.,2012(2):374—381.
APA	Song WJ,&Yulong Zhang, Weiyan Wang.(2012).The Solubility and Temperature Dependence of Resistivity for Aluminum-Doped Zinc Oxide Ceramic.Int. J. Appl. Ceram. Technol.(2),374—381.
MLA	Song WJ,et al."The Solubility and Temperature Dependence of Resistivity for Aluminum-Doped Zinc Oxide Ceramic".Int. J. Appl. Ceram. Technol. .2(2012):374—381.