Preparation of nanometer rutile TiO2 powder and its characteristics

CORC > 过程工程研究所 > 中国科学院过程工程研究所 > 研究所（批量导入）

	Preparation of nanometer rutile TiO2 powder and its characteristics
	Lin, YH ; Zhang, ZT ; Huang, SL ; Li, JL
刊名	JOURNAL OF INORGANIC MATERIALS
	1999-12-01
卷号	14 期号:6 页码:853-860
关键词	nanometer rutile TiO2 inoganic functional materials composite powders
ISSN号	1000-324X
其他题名	J. Inorg. Mater.
中文摘要	Nanometer rutile TiO2 is a new kind of inorganic functional material. its preparation and application have been paid more and more attention. In this study, ZnCO3 was used to coat on the surface of Ti(OH)(4), then heating to make ZnCO3 transfer to ZnO and Ti(OH)(4) transfer to H2TiO3 at 500 degrees C, dissolving about 97wt% coated ZnO powder. Finally,the rutile TiO2 powders were prepared after having calcined the H2TiO3 powder (containing 3wt%ZnO) at 800 degrees C, and the particle size was about 20 similar to 60nm obtained. The morphology, size, composition of rutile TiO2 powders were studied by means of TEM, ICP and XRD.
英文摘要	Nanometer rutile TiO2 is a new kind of inorganic functional material. its preparation and application have been paid more and more attention. In this study, ZnCO3 was used to coat on the surface of Ti(OH)(4), then heating to make ZnCO3 transfer to ZnO and Ti(OH)(4) transfer to H2TiO3 at 500 degrees C, dissolving about 97wt% coated ZnO powder. Finally,the rutile TiO2 powders were prepared after having calcined the H2TiO3 powder (containing 3wt%ZnO) at 800 degrees C, and the particle size was about 20 similar to 60nm obtained. The morphology, size, composition of rutile TiO2 powders were studied by means of TEM, ICP and XRD.
WOS标题词	Science & Technology ; Technology
类目[WOS]	Materials Science, Ceramics
研究领域[WOS]	Materials Science
收录类别	SCI
原文出处	://WOS:000084454600004
语种	英语
WOS记录号	WOS:000084454600004
公开日期	2013-11-15
内容类型	期刊论文
版本	出版稿
源URL	[http://ir.ipe.ac.cn/handle/122111/6027]
专题	过程工程研究所_研究所（批量导入）
作者单位	1.Tsing Hua Univ, Dept Mat Sci & Engn, Beijing 100084, Peoples R China 2.Chinese Acad Sci, Inst Chem Met, Beijing 100080, Peoples R China
推荐引用方式 GB/T 7714	Lin, YH,Zhang, ZT,Huang, SL,et al. Preparation of nanometer rutile TiO2 powder and its characteristics[J]. JOURNAL OF INORGANIC MATERIALS,1999,14(6):853-860.
APA	Lin, YH,Zhang, ZT,Huang, SL,&Li, JL.(1999).Preparation of nanometer rutile TiO2 powder and its characteristics.JOURNAL OF INORGANIC MATERIALS,14(6),853-860.
MLA	Lin, YH,et al."Preparation of nanometer rutile TiO2 powder and its characteristics".JOURNAL OF INORGANIC MATERIALS 14.6(1999):853-860.