Accelerated Life Test of Concrete Under Multiple Factors Based on Three-parameter Weibull Distribution | |
Qiao, Hongxia1; Guo, Xiangke1; Zhu, Binrong2 | |
刊名 | Cailiao Daobao/Materials Reports |
2019-02-25 | |
卷号 | 33期号:2页码:639-643 |
关键词 | Concrete testing Concretes Durability Environmental testing Underground corrosion Accelerated degradation Accelerated life tests Distribution fitting Durability evaluation Durability of concretes Dynamic modulus of elasticity Life predictions Three parameter Weibull distribution |
ISSN号 | 1005023X |
DOI | 10.11896/cldb.201904014 |
英文摘要 | Aiming at the extrusive problem of poor durability of concrete in saline soil area of western China, the indoor accelerated life test of concrete was designed to simulate natural environment, including halide corrosion, wet and dry cycle, freeze-thaw cycle and solar radiation. The dynamic modulus of elasticity was adopted as the to failure threshold to evaluate the durability of concrete, and the accelerated life data of concrete were obtained. Based on the three-parameter Weibull distribution, the probability analysis software was employed to analyze and predict the life data, and the distribution overview plot-arbitrary cens of accelerated life was acquired. It could be found from the results that the sample points of accelerated life data could be well fitted by three-parameter Weibull distribution. Moreover, the failure time of concrete durability degradation and reliability of accelerated degradation process could be directly reflected by its threshold parameter and distribution overview plot-arbitrary cens, respectively, which provides a novel reliability basis for durability evaluation of concrete. © 2019, Materials Review Magazine. All right reserved. |
语种 | 中文 |
出版者 | Cailiao Daobaoshe/ Materials Review |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/114296] |
专题 | 土木工程学院 |
作者单位 | 1.College of Civil Engineering, Lanzhou University of Technology, Lanzhou; 730050, China; 2.College of Civil Engineering, Southeast China University, Nanjing; 211189, China |
推荐引用方式 GB/T 7714 | Qiao, Hongxia,Guo, Xiangke,Zhu, Binrong. Accelerated Life Test of Concrete Under Multiple Factors Based on Three-parameter Weibull Distribution[J]. Cailiao Daobao/Materials Reports,2019,33(2):639-643. |
APA | Qiao, Hongxia,Guo, Xiangke,&Zhu, Binrong.(2019).Accelerated Life Test of Concrete Under Multiple Factors Based on Three-parameter Weibull Distribution.Cailiao Daobao/Materials Reports,33(2),639-643. |
MLA | Qiao, Hongxia,et al."Accelerated Life Test of Concrete Under Multiple Factors Based on Three-parameter Weibull Distribution".Cailiao Daobao/Materials Reports 33.2(2019):639-643. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论