Reliability analysis of freeze-thaw damage of fiber reinforced concrete based on miner theory | |
Jiangchuan, Li1; Hongxia, Qiao2; Feifei, Zhu1 | |
刊名 | Emerging Materials Research |
2019-09-01 | |
卷号 | 8期号:3页码:508-515 |
关键词 | Blending Durability Fiber reinforced materials Freezing Frost resistance Miners Polypropylenes Reliability analysis Reliability theory Steel fibers Thawing Concrete durability Degradation of fibers Environmental factors Fatigue cumulative damage Fiber-reinforced concretes Frost resistance performance Hybrid fiber concretes Reliability calculation |
ISSN号 | 20460147 |
DOI | 10.1680/jemmr.19.00028 |
英文摘要 | In the cold regions of the north China, due to special climatic and environmental factors, the degradation of concrete durability caused by freeze-thaw cycles has been a widespread concern among researchers. Freeze-thaw damage is considered to be the main form of damage that causes its durability to deteriorate. Aiming at the influence of freeze-thaw damage on the service life of concrete structures in building structures, The freeze-thaw test was carried out in this paper to study the frost resistance of the formed concrete under different fiber (steel fiber, polypropylene fiber) blending modes. The durability degradation of fiber concrete under different freeze-thaw cycles was analyzed, and its microstructure was evaluated by SEM. The study found that the frost resistance of single fiber concrete is not obvious, the frost resistance of the integral fiber concrete is greatly improved, and the layered hybrid fiber concrete has excellent frost resistance performance. In addition, based on the fatigue cumulative damage Miner theory, the reliability calculation model of freeze-thaw damage is established, which can directly reflect the relationship between the reliability of the test sample and the freeze-thaw cycle. The reliability of concrete with different fiber blending methods gradually decreases to varying degrees. This theory has good applicability in the reliability analysis of concrete freeze-thaw. © 2019 ICE Publishing: All rights reserved. |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ICE Publishing |
WOS记录号 | WOS:000488307500025 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/113880] |
专题 | 土木工程学院 |
作者单位 | 1.Eng. Res. Ctr. of the W. Min. of Educ. for Civ. Eng. of Disaster Prevention and Disaster Reduction, Lanzhou University of Technology, Lanzhou, China; 2.Key Laboratory of Disaster Prevention and Mitigation in Civil Engineering of Gansu Province, Lanzhou University of Technology, Lanzhou, China |
推荐引用方式 GB/T 7714 | Jiangchuan, Li,Hongxia, Qiao,Feifei, Zhu. Reliability analysis of freeze-thaw damage of fiber reinforced concrete based on miner theory[J]. Emerging Materials Research,2019,8(3):508-515. |
APA | Jiangchuan, Li,Hongxia, Qiao,&Feifei, Zhu.(2019).Reliability analysis of freeze-thaw damage of fiber reinforced concrete based on miner theory.Emerging Materials Research,8(3),508-515. |
MLA | Jiangchuan, Li,et al."Reliability analysis of freeze-thaw damage of fiber reinforced concrete based on miner theory".Emerging Materials Research 8.3(2019):508-515. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论