Adsorption and Photocatalysis Performance of Bi4Ti3O12 Nanoparticles Synthesized via a Polyacrylamide Gel Route | |
Cui, Z. M.; Yang, H.; Zhang, M.; Zhang, H. M.; Su, J. Y.; Li, R. S. | |
刊名 | MATERIALS TRANSACTIONS
![]() |
2016 | |
卷号 | 57期号:10页码:1766-1770 |
关键词 | Bi4Ti3O12 nanoparticles polyacrylamide gel route active species photocatalytic mechanism |
ISSN号 | 1345-9678 |
DOI | 10.2320/matertrans.M2016212 |
英文摘要 | A polyacrylamide gel route was adopted to synthesize Bi4Ti3O12 nanoparticles and the effect of chelating agents on the products was investigated. When citric acid and acetic acid is separately used as the chelating agent, single-phase Bi4Ti3O12 samples can be prepared at a calcination temperature of 500 degrees C; however, when tartaric acid or EDTA is used as the chelating agent, a higher calcination temperature of 600 degrees C is required to produce single-phase samples. SEM observation shows that the as-prepared samples are composed of sphere-like or ellipsoid-like particles. The average particle size of the citric acid-, acetic acid-, tartaric acid-, and EDTA-resulted samples is centered around 32, 35, 90 and 120 nm, respectively. The bandgap energy of the four samples is measured to be 3.27 eV by ultraviolet-visible diffuse reflectance spectroscopy. The photocatalytic activity of Bi4Ti3O12 samples was evaluated by degrading RhB under simulated-sunlight irradiation, and the influence of pH value on the adsorption and photocatalytic degradation of the dye was also investigated. Ethanol, BQ and AO were respectively used as the scavengers of center dot OH, center dot O-2(-) and h(+) to investigate their effect on the photocatalytic degradation with the aim of revealing the photocatalytic mechanism involved. Based on the experimental results, the direct oxidation by h(+) is suggested to be the main mechanism toward the dye degradation. |
资助项目 | National Natural Science Foundation of China[51262018] ; Hongliu Outstanding Talents Foundation of Lanzhou University of Technology[J201205] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | JAPAN INST METALS |
WOS记录号 | WOS:000388453000016 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/33807] ![]() |
专题 | 理学院 图书馆 |
通讯作者 | Yang, H. |
作者单位 | Lanzhou Univ Technol, Sch Sci, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Cui, Z. M.,Yang, H.,Zhang, M.,et al. Adsorption and Photocatalysis Performance of Bi4Ti3O12 Nanoparticles Synthesized via a Polyacrylamide Gel Route[J]. MATERIALS TRANSACTIONS,2016,57(10):1766-1770. |
APA | Cui, Z. M.,Yang, H.,Zhang, M.,Zhang, H. M.,Su, J. Y.,&Li, R. S..(2016).Adsorption and Photocatalysis Performance of Bi4Ti3O12 Nanoparticles Synthesized via a Polyacrylamide Gel Route.MATERIALS TRANSACTIONS,57(10),1766-1770. |
MLA | Cui, Z. M.,et al."Adsorption and Photocatalysis Performance of Bi4Ti3O12 Nanoparticles Synthesized via a Polyacrylamide Gel Route".MATERIALS TRANSACTIONS 57.10(2016):1766-1770. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论