An efficient flame retardant for epoxy resin: Preparation and pyrolytic behaviour | |
Yang, Baoping; Li, Xiang; Wang, Lurong; Zhang, Yabin; Cui, Jinfeng; Guo, Junhong; Tian, Li | |
刊名 | High Performance Polymers |
2019-11-01 | |
卷号 | 31期号:9-10页码:1009-1019 |
关键词 | Curing Epoxy resins Gas chromatography Mass spectrometry Phosphorus Scanning electron microscopy Smoke Cone calorimeter Flame retardancy High-efficiency Limited oxygen index Mass spectrometry analysis Phosphorous-containing flame retardants Scanning electron microscopy image Vertical burning tests |
ISSN号 | 09540083 |
DOI | 10.1177/0954008318815730 |
英文摘要 | Using 4,4-diaminodiphenyl methane as a curing agent, three kinds of monomers, 4,4′-dihydroxybenzophenone, diphenyl chlorophosphite and 1,4-phenylene diisocyanate (NCO), were introduced into a thermosetting resin (DGEBA). The flame retardancy properties of the composites were studied, and the results were compared with those of 5 wt% bis(bis(4-((diphenoxyphosphoryl)oxy)phenyl)methyl) 1,4-phenylenedicarbamate (DHPP-OH-NCO), 10 wt% DHPP-OH-NCO and 15 wt% DHPP-OH-NCO curing agents. The results showed that 15 wt% DHPP-OH-NCO had an improved flame retardancy, the limited oxygen index reached 33.5% and the vertical burning test (UL94) achieved a V-0 level. A cone calorimeter experiment showed that the addition of the flame retardant significantly reduced the amount of generated smoke and heat. Macroscopic digital images, scanning electron microscopy images and thermogravimetric analysis results further revealed that the epoxy resin (EP) with DHPP-OH-NCO exhibited greater char yields. The flame retardancy mechanism of the flame retardant was preliminarily shown by pyrolysis–gas chromatography–mass spectrometry analysis. The combined test results demonstrate that a high-efficiency phosphorous-containing flame retardant for EPs was successfully developed. © The Author(s) 2018. |
WOS研究方向 | Polymer Science |
语种 | 英语 |
出版者 | SAGE Publications Ltd |
WOS记录号 | WOS:000484947700001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/150462] |
专题 | 图书馆 石油化工学院 实验室建设与管理处 |
作者单位 | College of Petrochemical Technology, Lanzhou University of Technology, Lanzhou, China |
推荐引用方式 GB/T 7714 | Yang, Baoping,Li, Xiang,Wang, Lurong,et al. An efficient flame retardant for epoxy resin: Preparation and pyrolytic behaviour[J]. High Performance Polymers,2019,31(9-10):1009-1019. |
APA | Yang, Baoping.,Li, Xiang.,Wang, Lurong.,Zhang, Yabin.,Cui, Jinfeng.,...&Tian, Li.(2019).An efficient flame retardant for epoxy resin: Preparation and pyrolytic behaviour.High Performance Polymers,31(9-10),1009-1019. |
MLA | Yang, Baoping,et al."An efficient flame retardant for epoxy resin: Preparation and pyrolytic behaviour".High Performance Polymers 31.9-10(2019):1009-1019. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论