Preparation and performance evaluation of alumina sol prepared for FCC catalyst | |
Su, Kaimin1; Yin, Jianjun1; Zhang, Zhongdong2; Wang, Huili1; Meng, Yanzi1; Gao, Xionghou2 | |
刊名 | Huagong Xuebao/CIESC Journal |
2016-08-05 | |
卷号 | 67期号:8页码:3515-3520 |
关键词 | Alumina Aluminum Aluminum oxide Catalysts Colloids Fluid catalytic cracking pH Alumin Alumina content Aluminum powders Catalytic performance Cracking catalysts Peptization Physical and chemical properties Zeta potential analyzers |
ISSN号 | 04381157 |
DOI | 10.11949/j.issn.0438-1157.20160379 |
英文摘要 | The alumina sol with high content of Al2O3 was prepared by acidolysis-peptizing with aluminum as an additive. Its physical and chemical properties were characterized by pH meter, rheometer, digital viscometer and zeta potential analyzer. Catalytic performance of catalyst that was prepared with alumina sol was evaluated through a fixed-bed. The results showed that the alumina content can reach 20% (mass) of the alumina sol sample with aluminum powder pH of 2.3. The alumina sol had good stability and chlorine was not higher than 15% (mass), which can meet the FCC cracking catalyst requirements. © All Right Reserved. |
语种 | 中文 |
出版者 | Materials China |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/112770] |
专题 | 石油化工学院 |
作者单位 | 1.College of Petrochemical Engineering, Lanzhou University of Technology, Lanzhou; Gansu; 730050, China; 2.Lanzhou Petrochemical Research Center PetroChina, Lanzhou; Gansu; 730060, China |
推荐引用方式 GB/T 7714 | Su, Kaimin,Yin, Jianjun,Zhang, Zhongdong,et al. Preparation and performance evaluation of alumina sol prepared for FCC catalyst[J]. Huagong Xuebao/CIESC Journal,2016,67(8):3515-3520. |
APA | Su, Kaimin,Yin, Jianjun,Zhang, Zhongdong,Wang, Huili,Meng, Yanzi,&Gao, Xionghou.(2016).Preparation and performance evaluation of alumina sol prepared for FCC catalyst.Huagong Xuebao/CIESC Journal,67(8),3515-3520. |
MLA | Su, Kaimin,et al."Preparation and performance evaluation of alumina sol prepared for FCC catalyst".Huagong Xuebao/CIESC Journal 67.8(2016):3515-3520. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论