Effect of stress ratio on high cycle fatigue behavior of TNM-TiAl alloy | |
Sun, Guanze4; Cao, Rui4; Zhou, Xin4; Jiang, Xiao Xia2; Wang, Hongwei1,3 | |
刊名 | FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES |
2022-09-01 | |
关键词 | fracture mechanism high cycle fatigue stress ratio TNM-TiAl alloy |
ISSN号 | 8756-758X |
DOI | 10.1111/ffe.13835 |
英文摘要 | In order to investigate the effect of stress ratio on room temperature high-cycle fatigue life of Ti-43.5Al-4Nb-1Mo-0.1B alloy, high-cycle fatigue life test of TNM-TiAl alloy at stress ratio of -1, -0.5, 0.1, 0.5, 0.8, and 1 was performed on the universal testing machine. The fracture mechanism of TNM-TiAl alloy under different stress ratios was determined by observation and analysis of microstructure and fracture surface by scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), and optical microscope (OM). The results show that fatigue life of TNM-TiAl alloy with different stress ratios is mainly affected by the mean stress and stress amplitude. The fatigue life decreases with the increase of the stress amplitude and with the decrease of the mean stress. When the stress amplitude is constant, the higher the stress ratio is, the higher the mean stress in the loading process is, the lower the fatigue life is. The sensitivity of the stress amplitude of TNM-TiAl alloy gradually increases with the increase of the stress ratio. The different cracking mechanism and fracture mechanisms at various stress ratio are revealed. |
WOS研究方向 | Engineering ; Materials Science |
语种 | 英语 |
出版者 | WILEY |
WOS记录号 | WOS:000852977800001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/159847] |
专题 | 材料科学与工程学院 |
作者单位 | 1.Beijing CISRI Gaona Mat Technol Co Ltd, Beijing, Peoples R China; 2.Ningxia Univ, Sch Mech Engn, Yinchuan, Ningxia, Peoples R China; 3.Cent Iron & Steel Res Inst, Beijing Key Lab Adv High Temp Mat, Beijing, Peoples R China 4.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Dept Mat Sci & Engn, Langongping 287 Rd, Lanzhou 730050, Gansu, Peoples R China; |
推荐引用方式 GB/T 7714 | Sun, Guanze,Cao, Rui,Zhou, Xin,et al. Effect of stress ratio on high cycle fatigue behavior of TNM-TiAl alloy[J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES,2022. |
APA | Sun, Guanze,Cao, Rui,Zhou, Xin,Jiang, Xiao Xia,&Wang, Hongwei.(2022).Effect of stress ratio on high cycle fatigue behavior of TNM-TiAl alloy.FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES. |
MLA | Sun, Guanze,et al."Effect of stress ratio on high cycle fatigue behavior of TNM-TiAl alloy".FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES (2022). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论