Influence of Media on Oxidation Film in High Temperature Corrosion of GH3625 Alloy | |
Ma Yuanjun1,2; Ding Yutain1,2; Liu Jianjun1,2; Gao Yubi1,2; Chen Jianjun1,2; Wang Xingmao1,2 | |
刊名 | RARE METAL MATERIALS AND ENGINEERING |
2022-05-01 | |
卷号 | 51期号:5页码:1713-1723 |
关键词 | GH3625 alloy high temperature corrosion corrosive medium oxide film corrosion mechanism |
ISSN号 | 1002-185X |
英文摘要 | The corrosion behavior of as-cast GH3625 alloy were studied in different corrosive media (Air, 75wt%Na2SO4+25wt%NaCl and 2%SO2+H2O+Air) at 900 degrees C for 120 h, utilizing XRD, SEM, EDS, mass-gain measurement and thermodynamic calculation. The formation and destruction mechanism of the oxide film under different corrosive media were discussed. Results show that from the top layer to the internal structure of GH3625 alloy is divided into loose oxide layer, dense oxide layer, Cr poor zone and alloy matrix after corrosion in different media, and the oxide layer is mainly composed of NiO, Cr2O3 and NiCr2O4. In addition, the depth of Cr-poor zone after corrosion in corrosive medium (14 mu m and 11 mu m) is greater than that after oxidation in air (8 mu m). The damage degree of corrosion medium to the surface oxide film of the alloy is molten salt medium, acidic atmosphere medium and air medium in descending order. The corrosion of GH3625 alloy is mainly due to the competition between the formation and dissolution of the surface oxide film in different media. When GH3625 alloy is corroded in 75wt%Na2SO4+25wt%NaCl medium, the corrosion mechanism is mainly that the oxide film reacts with Cl- to form gas phase Cl-2 and reacts with Na2O to form chromate Na2CrO4. However, when GH3625 alloy is corroded in 2%SO2+H2O+Air, the corrosion mechanism is mainly the continuous sulfurization and oxidation reaction of Cr, Ni and SO2, O-2. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 中文 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
WOS记录号 | WOS:000813756100025 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/158828] |
专题 | 材料科学与工程学院 |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China; 2.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Ma Yuanjun,Ding Yutain,Liu Jianjun,et al. Influence of Media on Oxidation Film in High Temperature Corrosion of GH3625 Alloy[J]. RARE METAL MATERIALS AND ENGINEERING,2022,51(5):1713-1723. |
APA | Ma Yuanjun,Ding Yutain,Liu Jianjun,Gao Yubi,Chen Jianjun,&Wang Xingmao.(2022).Influence of Media on Oxidation Film in High Temperature Corrosion of GH3625 Alloy.RARE METAL MATERIALS AND ENGINEERING,51(5),1713-1723. |
MLA | Ma Yuanjun,et al."Influence of Media on Oxidation Film in High Temperature Corrosion of GH3625 Alloy".RARE METAL MATERIALS AND ENGINEERING 51.5(2022):1713-1723. |
个性服务 |
查看访问统计 |
相关权益政策 |