Precipitation and Growth Behavior of Magnetite Crystal During Continuous Cooling of Molten Nickel Oxide Slag | |
Li Bin; Du Xueyan; Shen Yingying | |
刊名 | RARE METAL MATERIALS AND ENGINEERING |
2022-05-01 | |
卷号 | 51期号:5页码:1821-1827 |
关键词 | nickel slag molten oxidation magnetite crystal HT-CLSM in-situ observation |
ISSN号 | 1002-185X |
英文摘要 | The efficient extraction of iron from nickel slag has attracted more recent attention in the recycling of nickel slag. In this research, Factsage software was used to predict the formation and preferential precipitation behavior of magnetite crystal in molten nickel oxide slag. The precipitation and growth of magnetite crystal in molten nickel oxide slag during continuous cooling were in-situ observed by high temperature laser confocal microscope (HT-CLSM), and the growth characteristics of magnetite crystal under 5 similar to 50 degrees C/min cooling rate was studied. The morphology, phase and composition of the samples were characterized by SEM-EDS, XRD and ICP. The results show that magnetite crystals are preferentially precipitated from the melt during continuous cooling, and the initial precipitation temperature is between 1430 similar to 1450 degrees C. At low cooling rate (5 similar to 15 degrees C/min), the initial nucleation and precipitation of the crystals are slow, and the grains grow stably at 1200 similar to 1400 degrees C, with an average growth rate of 0.141 gin/s, and the final grain size is more than 100 mu m. High cooling rate (25 similar to 50 degrees C/min) can promote the rapid nucleation and precipitation of magnetite crystal at the initial stage of growth, but the stable growth rate is small, and the final grain size is 20 similar to 30 mu m. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 中文 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
WOS记录号 | WOS:000813756100038 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/158823] |
专题 | 材料科学与工程学院 研究生院 |
作者单位 | Lanzhou Univ Technol, Sch Mat Sci & Engn, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Li Bin,Du Xueyan,Shen Yingying. Precipitation and Growth Behavior of Magnetite Crystal During Continuous Cooling of Molten Nickel Oxide Slag[J]. RARE METAL MATERIALS AND ENGINEERING,2022,51(5):1821-1827. |
APA | Li Bin,Du Xueyan,&Shen Yingying.(2022).Precipitation and Growth Behavior of Magnetite Crystal During Continuous Cooling of Molten Nickel Oxide Slag.RARE METAL MATERIALS AND ENGINEERING,51(5),1821-1827. |
MLA | Li Bin,et al."Precipitation and Growth Behavior of Magnetite Crystal During Continuous Cooling of Molten Nickel Oxide Slag".RARE METAL MATERIALS AND ENGINEERING 51.5(2022):1821-1827. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论