Interfacial Characteristics of 6061/AZ31B Composites in Multi-Pass Rolling | |
Yang, Haokun1; Li, Yuandong1,2; Qiu, Jin1; Song, Zhaoxi1; Bi, Guangli1,2; Zhou, Hongwei1 | |
刊名 | Materials |
2022-02-01 | |
卷号 | 15期号:3 |
关键词 | Aluminum alloys Magnesium alloys Plates (structural components) Rolling Tensile strength 6061 aluminum alloys Al 6061 AZ31B magnesium alloys Bonding layers Composite plates Interface organization Interfacial characteristics Multi-pass rolling Recrystallisation Solid/liquid |
DOI | 10.3390/ma15031199 |
英文摘要 | An Al 6061/Mg AZ31B composite plate with good bonding and excellent comprehensive mechanical properties was prepared through solid-liquid cast-rolling bonding (SLCRB). The mi-crostructure evolution and mechanical behavior of Al/Mg composite plates under different rolling passes were studied. The results showed that with the increase of rolling passes, the bonding layer of the composite plate was crushed, and the base material on both sides of the substrate gradually grew towards the broken part of the bonding layer. The microstructure on both sides of the substrate extended along the rolling direction and was dynamically recrystallized to a certain extent. In the Mg substrate, because the preheating temperature was higher than its recrystallization tem-perature, with the increase of rolling passes, the grains in Mg substrate were crystallized. When the rolling passes reached the fourth pass, complete recrystallization basically took place in the Mg substrate. With the change of the internal structure and bonding layer on both sides of the sub-strate, the mechanical properties of the composite plate can be improved gradually. The tensile strength increased from 136 MPa before rolling to 190 MPa at the fourth pass, and the shear strength increased from 74 MPa to 98 MPa, with growth rates of about 40% and 32%, respectively. The elongation of the composite plate decreased from 6.3% to 5.4%, a decrease of about 1%. © 2022 by the authors. Licensee MDPI, Basel, Switzerland. |
语种 | 英语 |
出版者 | MDPI |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/157961] |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Key Laboratory of Non-Ferrous Metal Alloys and Processing, Ministry of Education, Lanzhou University of Technology, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Yang, Haokun,Li, Yuandong,Qiu, Jin,et al. Interfacial Characteristics of 6061/AZ31B Composites in Multi-Pass Rolling[J]. Materials,2022,15(3). |
APA | Yang, Haokun,Li, Yuandong,Qiu, Jin,Song, Zhaoxi,Bi, Guangli,&Zhou, Hongwei.(2022).Interfacial Characteristics of 6061/AZ31B Composites in Multi-Pass Rolling.Materials,15(3). |
MLA | Yang, Haokun,et al."Interfacial Characteristics of 6061/AZ31B Composites in Multi-Pass Rolling".Materials 15.3(2022). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论