Enhanced Mechanical Properties of 316L Stainless Steel Prepared by Aluminothermic Reaction Subjected to Multiple Warm Rolling | |
Li, Z.N.1; Wei, F.A.2; La, P.Q.1; Ma, F.L.1 | |
刊名 | Metals and Materials International |
2018-05-01 | |
卷号 | 24期号:3页码:633-643 |
关键词 | Austenite Dynamic recrystallization Microstructure Nanocrystals Rolling Tensile strength |
ISSN号 | 15989623 |
DOI | 10.1007/s12540-018-0066-y |
英文摘要 | Large dimensional bulk 316L stainless steels were prepared by aluminothermic reaction method and rolled at 973 K (700 °C) with different deformation, the microstructures evolution and mechanical properties were characterized in detail. The results showed that the microstructure of casting steel consists of nanocrystalline/submicrocrystalline/microcrystalline austenite and submicrocrystalline ferrite. After rolling to thickness reduction of 30, 50 and 70%, the submicrocrystalline austenite grains were crushed and dispersed more uniformly in the matrix of the steel, the grain size of submicrocrystalline austenite decreased from 246 to 136 nm. The mechanical properties of the rolled steels were significantly enhanced, with the thickness reduction increased from 30 to 70%, the tensile strength increased from 632 to 824 MPa, the yield strength increased from 425 to 615 MPa, and the elongation increased from 11 to 24%. After rolling to thickness reduction of 70%, the optimized combination of high strength and high ductility was obtained. © 2018, The Korean Institute of Metals and Materials. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | Korean Institute of Metals and Materials |
WOS记录号 | WOS:000431506500021 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/151204] |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 2.Qinghai Provincial Key Laboratory of New Light Alloys, Qinghai Provincial Engineering, Research Center of High Performance Light Metal Alloys and Forming, Qinghai University, Xining; 810016, China |
推荐引用方式 GB/T 7714 | Li, Z.N.,Wei, F.A.,La, P.Q.,et al. Enhanced Mechanical Properties of 316L Stainless Steel Prepared by Aluminothermic Reaction Subjected to Multiple Warm Rolling[J]. Metals and Materials International,2018,24(3):633-643. |
APA | Li, Z.N.,Wei, F.A.,La, P.Q.,&Ma, F.L..(2018).Enhanced Mechanical Properties of 316L Stainless Steel Prepared by Aluminothermic Reaction Subjected to Multiple Warm Rolling.Metals and Materials International,24(3),633-643. |
MLA | Li, Z.N.,et al."Enhanced Mechanical Properties of 316L Stainless Steel Prepared by Aluminothermic Reaction Subjected to Multiple Warm Rolling".Metals and Materials International 24.3(2018):633-643. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论