Simultaneously enhancing the strength and ductility of particulate-reinforced aluminum matrix composite by aging treatment | |
Zhang, Xuezheng1,2; Chen, Tijun1 | |
刊名 | JOURNAL OF MATERIALS RESEARCH |
2021-09-14 | |
卷号 | 36期号:17页码:3445-3459 |
关键词 | Aluminum Composite Ductility Powder processing Strength |
ISSN号 | 0884-2914 |
DOI | 10.1557/s43578-021-00389-x |
英文摘要 | In this work, powder thixoforming technique was utilized to prepare 10 vol% SiC particulate-reinforced 6061 alloy matrix (SiCp/6061Al) composite and artificial aging treatment was conducted to enhance mechanical properties. The results reveal that the aging process of SiCp/6061Al composite at 175 degrees C can be divided into three stages: under-aged (0.5-10 h) stage, peak-aged (10 h) stage and over-aged (10-48 h) stage, which were dominated by Guinier-Preston zone, beta '' and beta phase, respectively. Correspondingly, the tensile strengths of this composite exhibited a trend of first rising (0.5-10 h) and then decreasing (10-48 h), while the elongation continuously decreased all the time. Comparing with the as-fabricated composite, optimal aging treatment for 10 h led to maximum ultimate tensile strength of 309 MPa, yield strength of 240 MPa and a moderate elongation of 3.7%, representing remarkable increments of 34.3%, 87.5% and 42.3%, respectively. The aging behaviors of SiCp/6061Al composite and corresponding strengthening as well as toughening mechanisms were discussed. Graphic abstract |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | SPRINGER HEIDELBERG |
WOS记录号 | WOS:000709849300006 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/150054] |
专题 | 材料科学与工程学院 |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China; 2.Dongguan Eontec Co Ltd, Dongguan 523662, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Xuezheng,Chen, Tijun. Simultaneously enhancing the strength and ductility of particulate-reinforced aluminum matrix composite by aging treatment[J]. JOURNAL OF MATERIALS RESEARCH,2021,36(17):3445-3459. |
APA | Zhang, Xuezheng,&Chen, Tijun.(2021).Simultaneously enhancing the strength and ductility of particulate-reinforced aluminum matrix composite by aging treatment.JOURNAL OF MATERIALS RESEARCH,36(17),3445-3459. |
MLA | Zhang, Xuezheng,et al."Simultaneously enhancing the strength and ductility of particulate-reinforced aluminum matrix composite by aging treatment".JOURNAL OF MATERIALS RESEARCH 36.17(2021):3445-3459. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论