Isothermal oxidation and TGO growth behaviors of YAG/YSZ double-ceramic-layer thermal barrier coatings | |
An, Guosheng1,2; Li, Wensheng1,2; Feng, Li1,2; Cheng, Bo1,2; Wang, Zhiping1; Li, Ziyu1; Zhang, Yi1 | |
刊名 | CERAMICS INTERNATIONAL |
2021-09-01 | |
卷号 | 47期号:17页码:24320-24330 |
关键词 | YAG/YSZ TBC TGO High temperature oxidation resistance Oxygen ionic diffusion |
ISSN号 | 0272-8842 |
DOI | 10.1016/j.ceramint.2021.05.144 |
英文摘要 | In this study, yttrium aluminum garnet/yttria-stabilized zirconia (YAG/YSZ) double-ceramic-layer thermal barrier coatings (DCL TBC) and yttria-stabilized zirconia (YSZ) single-ceramic-layer thermal barrier coatings (SCL TBC) were deposited by atmosphere plasma spray (APS) on the Inconel 738 alloy substrate, and isothermal oxidation tests were performed to investigate the formation and growth behavior of thermally grown oxide (TGO). Results showed that the Al2O3 TGO thickness of both TBC groups increased by increasing the isothermal oxidation time,and then slowly decreased with the appearance and growth of the adverse multilayer structure comprising CoCr2O4, (Ni,Co)Al2O4, NiCr2O4, and NiO mixed oxides. However, since the significant inhibition effect of the YAG coating to oxygen ionic diffusion, the mixed oxides appearance time and TGO growth behaviors were delayed in the DCL TBC. As a result, the TGO thickness of the DCL TBC was always smaller than that of the SCL TBC in the entire oxidation process. And the Al2O3 layer thickness proportion in the total TGO of the DCL TBC was greater than or equal to that of the SCL TBC after oxidation for the same period. The results of weight gain showed that compared with the SCL TBC, the parabolic oxidation rate of the DCL TBC was decreased approximately 35%. Consequently, the DCL TBC has better high-temperature oxidation resistance than the SCL TBC. |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000677906900004 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/148561] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
作者单位 | 1.Lanzhou Univ Technol, Sch Mat Sci & Engn, Lanzhou 730050, Gansu, Peoples R China 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China; |
推荐引用方式 GB/T 7714 | An, Guosheng,Li, Wensheng,Feng, Li,et al. Isothermal oxidation and TGO growth behaviors of YAG/YSZ double-ceramic-layer thermal barrier coatings[J]. CERAMICS INTERNATIONAL,2021,47(17):24320-24330. |
APA | An, Guosheng.,Li, Wensheng.,Feng, Li.,Cheng, Bo.,Wang, Zhiping.,...&Zhang, Yi.(2021).Isothermal oxidation and TGO growth behaviors of YAG/YSZ double-ceramic-layer thermal barrier coatings.CERAMICS INTERNATIONAL,47(17),24320-24330. |
MLA | An, Guosheng,et al."Isothermal oxidation and TGO growth behaviors of YAG/YSZ double-ceramic-layer thermal barrier coatings".CERAMICS INTERNATIONAL 47.17(2021):24320-24330. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论