Microstructural evolution and age-hardening behavior of quasicrystal-reinforced Mg–Dy–Zn alloy | |
Bi, Guang-Li1,2; Han, Yu-Xiang1,2; Jiang, Jing1,2; Jiang, Chun-Hong1,2,3; Li, Yuan-Dong1,2; Ma, Ying1,2 | |
刊名 | Rare Metals |
2019-08-12 | |
卷号 | 38期号:8页码:739-745 |
关键词 | Age hardening Binary alloys Dysprosium alloys Hardening Magnesium alloys Microstructural evolution Microstructure Precipitation (chemical) Solid solutions Ternary alloys Tungsten alloys Age hardening behaviors Aging treatment As cast alloy Co-precipitates I-phase Solid solution and aging treatments Solid solution treatment Zn alloys |
ISSN号 | 10010521 |
DOI | 10.1007/s12598-018-1089-8 |
英文摘要 | Microstructural evolution and age-hardening behavior of Mg–2Dy–6Zn (at%) alloy during solid-solution and aging treatment were investigated. The microstructure of as-cast alloy is composed of α-Mg, Mg3DyZn6 (I) phase, Mg3Dy2Zn3 (W) phase, Mg(Zn,Dy) phase and a small amount of Mg0.97Zn0.03 phases. After solid-solution treatment (480 °C, 12 h), all the I phases and most W phases dissolve into α-Mg matrix and the remainder W phases transform into Mg(Dy,Zn) phase and MgDy3 phase. During aging treatment, I phase and small amounts of W phases co-precipitate from α-Mg matrix, respectively. The alloy exhibits a peak hardness of HV 77.5 at 200 °C for 8 h. The excellent age-hardening behavior of alloy is mainly attributed to the co-precipitation strengthening of I and W phases. © 2018, The Nonferrous Metals Society of China and Springer-Verlag GmbH Germany, part of Springer Nature. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | University of Science and Technology Beijing |
WOS记录号 | WOS:000473188900004 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/114256] |
专题 | 材料科学与工程学院 |
作者单位 | 1.Key Laboratory of Nonferrous Metal Alloys and Processing, Ministry of Education, Lanzhou University of Technology, Lanzhou; 730050, China; 2.State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 3.Lanshi Foundry Co., Ltd., Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Bi, Guang-Li,Han, Yu-Xiang,Jiang, Jing,et al. Microstructural evolution and age-hardening behavior of quasicrystal-reinforced Mg–Dy–Zn alloy[J]. Rare Metals,2019,38(8):739-745. |
APA | Bi, Guang-Li,Han, Yu-Xiang,Jiang, Jing,Jiang, Chun-Hong,Li, Yuan-Dong,&Ma, Ying.(2019).Microstructural evolution and age-hardening behavior of quasicrystal-reinforced Mg–Dy–Zn alloy.Rare Metals,38(8),739-745. |
MLA | Bi, Guang-Li,et al."Microstructural evolution and age-hardening behavior of quasicrystal-reinforced Mg–Dy–Zn alloy".Rare Metals 38.8(2019):739-745. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论