Wear behavior of Ni-base composite coating with directional solidification structure | |
Yang, Guirong1; Zhao, Hu1; Song, Wenming1,2; Li, Jian3; Ma, Ying1 | |
刊名 | Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research |
2013-06-01 | |
卷号 | 27期号:3页码:279-286 |
关键词 | Composite coatings Composite materials Friction Microstructure Sintering Solidification Friction coefficients Friction wear properties Influential factors Metal solidification Self lubricating coating Testing parameters Tribological properties Vacuum fusion sintering |
ISSN号 | 10053093 |
英文摘要 | The composite 20%WC + Ni and 5%G + 20%WC+Ni coatings were prepared by vacuum cladding method on the ZG45 substrate. Microstructures, forming mechanism for the coatings and the tribological properties were investigated. The results show that the microstructure of composite coating is dense, and there are not any inclusion and pores at the interface of the coating and substrate. The main composition of coating is Ni-based solid solution and hard intermetalic compounds. The major influential factor of the isomeric microstructure is the directional solidification during metal solidification. The wear results show that the friction coefficient and fluctuation of friction coefficient of 5%G + 20%WC + Ni coating are lower than that of 20%WC + Ni coating for the same wearing testing parameters. The wear rate of 20%WC + Ni coating increases with the increasing wear frequency, whereas the wear rate of 5%G + 20% WC + Ni coating decreases with the increasing wear frequency. The abrasive wear and oxidation wear dominate the wearing process of 20%WC + Ni coating, and the oxidation wear and micro-crack lamellar for 5%G+20%WC+Ni coating. © Copyright. |
语种 | 中文 |
出版者 | Chinese Journal of Materials Research |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/113767] |
专题 | 材料科学与工程学院 |
作者单位 | 1.State Key Lab of Gansu Adv Non-ferrous Metal Mat and Key Lab of Non-ferrous Metal Alloys and Proc, The Ministry of Education, Lanzhou University of Technology, Lanzhou 730050, China; 2.Lanpec Technologies Limited, Lanzhou 730070, China; 3.Wuhan Research Institute of Materials Protection, Wuhan 430030, China |
推荐引用方式 GB/T 7714 | Yang, Guirong,Zhao, Hu,Song, Wenming,et al. Wear behavior of Ni-base composite coating with directional solidification structure[J]. Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research,2013,27(3):279-286. |
APA | Yang, Guirong,Zhao, Hu,Song, Wenming,Li, Jian,&Ma, Ying.(2013).Wear behavior of Ni-base composite coating with directional solidification structure.Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research,27(3),279-286. |
MLA | Yang, Guirong,et al."Wear behavior of Ni-base composite coating with directional solidification structure".Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research 27.3(2013):279-286. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论