Characteristics of TIG arc-assisted laser welding–brazing joint of aluminum to galvanized steel with preset filler powder | |
Li, Chun-Ling; Fan, Ding; Wang, Bin | |
刊名 | Rare Metals |
2015-09-19 | |
卷号 | 34期号:9页码:650-656 |
关键词 | Aluminum compounds Binary alloys Brazing Electric welding Fillers Galvanized metal Galvanizing Inert gases Intermetallics Iron alloys Laser beam welding Liquid metals Mechanical properties Phase interfaces Powder metals Steel Tensile strength 5a06 aluminum alloys Filler powders Galvanized steels Interface reactions Interfacial layer Steel substrate Tungsten inert gas Welding current |
ISSN号 | 10010521 |
DOI | 10.1007/s12598-015-0539-9 |
英文摘要 | Tungsten inert gas (TIG) arc-assisted laser welding–brazing was used for the butt joining of 5A06 aluminum alloy to the galvanized steel by preset filler powder without groove. The spreading behavior of liquid metal on the back of the galvanized steel at different assisted welding currents was also investigated. The results show that the assisted TIG arc optimizes the interface reaction temperature, enhances the wettability of liquid metal on the steel side, and forms a sound butt joint at an appropriate welding current. A non-uniform intermetallic compound is formed at the interfacial layer, which is composed of Fe2Al5 close to the steel substrate and Fe4Al13 close to the solidified aluminum. The superior tensile strength of joint is indicated when the welding current ranges from 13 to 16 A. The average tensile strength can reach 151 MPa at the welding current of 16 A, and the corresponding fracture belongs to the ductile and brittle hybrid mode. © 2015, The Nonferrous Metals Society of China and Springer-Verlag Berlin Heidelberg. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | University of Science and Technology Beijing |
WOS记录号 | WOS:000359949500006 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/112822] |
专题 | 机电工程学院 材料科学与工程学院 |
作者单位 | State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China |
推荐引用方式 GB/T 7714 | Li, Chun-Ling,Fan, Ding,Wang, Bin. Characteristics of TIG arc-assisted laser welding–brazing joint of aluminum to galvanized steel with preset filler powder[J]. Rare Metals,2015,34(9):650-656. |
APA | Li, Chun-Ling,Fan, Ding,&Wang, Bin.(2015).Characteristics of TIG arc-assisted laser welding–brazing joint of aluminum to galvanized steel with preset filler powder.Rare Metals,34(9),650-656. |
MLA | Li, Chun-Ling,et al."Characteristics of TIG arc-assisted laser welding–brazing joint of aluminum to galvanized steel with preset filler powder".Rare Metals 34.9(2015):650-656. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论