Effect of carbon content on microstructure and mechanical properties of nanostructure white cast iron | |
La, Pei-Qing; Zhen, Xiao-Juan; Hu, Su-Lei; Li, Cui-Ling; Wei, Yu-Peng; Lu, Xue-Feng; Wang, Hong-Ding; Wei, Fu-An | |
刊名 | Fenmo Yejin Cailiao Kexue yu Gongcheng/Materials Science and Engineering of Powder Metallurgy |
2014-06-01 | |
卷号 | 19期号:3页码:421-426 |
关键词 | Alloying elements Carbides Compression testing Compressive strength Mechanical properties Microstructure Nanostructures Ore pellets Pearlite Tensile strength Aluminothermic reactions Carbon content Effect of carbons Lamellar pearlite Microstructure and mechanical properties Microstructures and mechanical properties Tension and compression White cast irons |
ISSN号 | 16730224 |
英文摘要 | The nanostructure white cast irons without expensive elements were prepared by aluminothermic reaction, the effect of carbon content on its microstructures and mechanical properties was studied by XRD, OM, SEM, tension and compression test. The results show that, the white cast irons consist of pearlite with different shapes and cementite, the lamellar pearlite decreases and granular pearlite increases with increasing the carbon content. The average lamellar spacing of the pearlite phase is 165, 231 and 250 nm, respectively. With increasing carbon content, the vickers hardness of nanostructure white cast iron is 552, 577 and 575 HV, compressive strength is 2224, 2460 and 2220 MPa, and tensile strength is 383, 416 and 245 MPa, respectively, which are all first increases and then decreases with increasing carbon content; the elongation rate is 3%, 2.5% and 1%. The mechanical properties of nanostructure white cast iron without expensive alloying elements are the same to Ni-Hard2 cast iron. |
语种 | 中文 |
出版者 | Central South University |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/112742] |
专题 | 材料科学与工程学院 |
作者单位 | State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou 730050, China |
推荐引用方式 GB/T 7714 | La, Pei-Qing,Zhen, Xiao-Juan,Hu, Su-Lei,et al. Effect of carbon content on microstructure and mechanical properties of nanostructure white cast iron[J]. Fenmo Yejin Cailiao Kexue yu Gongcheng/Materials Science and Engineering of Powder Metallurgy,2014,19(3):421-426. |
APA | La, Pei-Qing.,Zhen, Xiao-Juan.,Hu, Su-Lei.,Li, Cui-Ling.,Wei, Yu-Peng.,...&Wei, Fu-An.(2014).Effect of carbon content on microstructure and mechanical properties of nanostructure white cast iron.Fenmo Yejin Cailiao Kexue yu Gongcheng/Materials Science and Engineering of Powder Metallurgy,19(3),421-426. |
MLA | La, Pei-Qing,et al."Effect of carbon content on microstructure and mechanical properties of nanostructure white cast iron".Fenmo Yejin Cailiao Kexue yu Gongcheng/Materials Science and Engineering of Powder Metallurgy 19.3(2014):421-426. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论