Effects of heat treatment after welding on friction stir welding joints of high-strength aluminum alloy
Wang, Xi-Jing1,2; Sun, Gui-Ping1,2; Zhang, Jie1,2; Xu, Cheng1,2; Li, Shu-Wei1,2; Niu, Yong1,2
刊名Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals
2009-03-01
卷号19期号:3页码:484-489
关键词After-heat treatment Aluminum alloys Fracture mechanics Friction High strength alloys Microstructure Research laboratories Tensile strength Textures 7075 aluminum alloy Effects of heat treatment Experimental conditions Friction stir welding joints High strength aluminum alloys Microstructure and properties Strengthening phase Thermomechanically affected zones
ISSN号10040609
英文摘要The microstructure and property before and after heat treatment of friction stir welded 5 mm aero 7075 aluminum alloy were investigated. The results show that when the rotating speed of stirring joint is 600 r/min and the welding speed is 60 mm/min, the tensile strength can reach 381 MPa that is 84.6% of the base metals, which are regarded as the most ideal parameters under experimental conditions. There are equiaxed grains with size of 6-7 μm in weld nugget. After heat treatment, the tensile strength can reach 415 MPa. The lowest hardness appears in thermomechanically affected zone (TMAZ) of advancing side. The fractography has a characteristic of dimples of strengthening phase and the strain fracture appears in TMAZ of advancing side of joints. The weak point of friction stir welding joint for 7075 aluminum alloy occurs in the TMAZ.
语种中文
出版者Central South University of Technology
内容类型期刊论文
源URL[http://ir.lut.edu.cn/handle/2XXMBERH/111599]  
专题材料科学与工程学院
机电工程学院
作者单位1.State Key Laboratory of Advanced Non-Ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China;
2.School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou 730050, China
推荐引用方式
GB/T 7714
Wang, Xi-Jing,Sun, Gui-Ping,Zhang, Jie,et al. Effects of heat treatment after welding on friction stir welding joints of high-strength aluminum alloy[J]. Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,2009,19(3):484-489.
APA Wang, Xi-Jing,Sun, Gui-Ping,Zhang, Jie,Xu, Cheng,Li, Shu-Wei,&Niu, Yong.(2009).Effects of heat treatment after welding on friction stir welding joints of high-strength aluminum alloy.Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals,19(3),484-489.
MLA Wang, Xi-Jing,et al."Effects of heat treatment after welding on friction stir welding joints of high-strength aluminum alloy".Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals 19.3(2009):484-489.
个性服务
查看访问统计
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。


©版权所有 ©2017 CSpace - Powered by CSpace