Effect of Cooling Rate on Microstructure and Properties of Heat-treated Fe(3)Al Intermetallics | |
Li, Yamin; Liu, Hongjun; Hao, Yuan | |
2011 | |
关键词 | Fe(3)Al Cooling Rate Heat Treatment Microstructure Property |
卷号 | 189-193 |
DOI | 10.4028/www.scientific.net/AMR.189-193.3891 |
页码 | 3891-3894 |
英文摘要 | The casting Fe(3)Al intermetallics were solidified in sodium silicate sand mould and permanent mould respectively to get different cooling rates. After heat treatment (1000 degrees C/15 h homogenizing annealing + furnace cooling followed by 600 degrees C/1 h tempering + oil quenching), the microstructure and properties of Fe(3)Al intermetallics were investigated. The results show that the heat-treated Fe(3)Al intermetallics at higher cooling rate has finer grained microstructure than lower cooling rate, and the lattice distortion increases due to the higher solid solubility of the elements Cr and B at higher cooling rate. The tensile strength and hardness of the Fe(3)Al intermetallics at higher cooling rate are slightly higher also. However, the impact power of intermetallics at higher cooling rate is 67.5% higher than that at lower cooling rate, and the impact fracture mode is also transformed from intercrystalline fracture at lower cooling rate to intercrystallin+transcrystalline mixed fracture at higher cooling rate. |
会议录 | MANUFACTURING PROCESS TECHNOLOGY, PTS 1-5 |
会议录出版者 | TRANS TECH PUBLICATIONS LTD |
会议录出版地 | LAUBLSRUTISTR 24, CH-8717 STAFA-ZURICH, SWITZERLAND |
语种 | 英语 |
WOS研究方向 | Engineering ; Materials Science |
WOS记录号 | WOS:000292279502059 |
内容类型 | 会议论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/37387] |
专题 | 国际教育学院 材料科学与工程学院 |
通讯作者 | Li, Yamin |
作者单位 | Lanzhou Univ Technol, Minist Educ, Key Lab Nonferrous Met Alloys & Proc, Lanzhou 730050, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Yamin,Liu, Hongjun,Hao, Yuan. Effect of Cooling Rate on Microstructure and Properties of Heat-treated Fe(3)Al Intermetallics[C]. 见:. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论