Microstructure Evolution of Al-Ti-C Alloy Wires during Remelting Process | |
Ding, Wanwu; Zhu, Jiangtao; Zhao, Wenjun; Xia, Tiandong | |
2013 | |
关键词 | Al-Ti-C Alloy TiC TiAl3 Microstructure Remelting |
卷号 | 652-654 |
DOI | 10.4028/www.scientific.net/AMR.652-654.1119 |
页码 | 1119-1123 |
英文摘要 | The regular pattern of evolution of TiC and TiAl3 during the remelting process of Al-Ti-C alloy wires was analyzed and the impact mechanism was discussed. The results show that: when the temperature of the remelting mass is at 730 degrees C, with the increase of the heat preservation time of remelting, the degree of agglomeration of the original dispersed TiC will increase, and they are pushed toward crystal boundaries by alpha-Al during the solidification process, while TiAl3 will dissolve, aggregate, and grow. When the remelting temperature is at 1000 degrees C, as the heat preservation time increases, not only the agglomeration degree of TiC increases significantly compared to that at 730 degrees C and the sizes and shapes of TiAl3 change significantly as well. The morphology of TiAl3 will change from being lump-and-short-rod-like to needle-and-flake-like. Before and after remelting, the Al-Ti-C alloys are both composed of TiAl3 and TiC, with no other phases formed. |
会议录 | ADVANCES IN MATERIALS AND MATERIALS PROCESSING, PTS 1-3 |
会议录出版者 | TRANS TECH PUBLICATIONS LTD |
会议录出版地 | LAUBLSRUTISTR 24, CH-8717 STAFA-ZURICH, SWITZERLAND |
语种 | 英语 |
WOS研究方向 | Engineering ; Materials Science |
WOS记录号 | WOS:000320475900224 |
内容类型 | 会议论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/36858] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | Ding, Wanwu |
作者单位 | Lanzhou Univ Technol, State Key Lab Gansu Adv Nonferrous Met Mat, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Ding, Wanwu,Zhu, Jiangtao,Zhao, Wenjun,et al. Microstructure Evolution of Al-Ti-C Alloy Wires during Remelting Process[C]. 见:. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论