Enhanced intergranular corrosion resistance and tensile strength in 304 stainless steel with dispersed nanocrystallines in microcrystalline austenite | |
Wei, Fuan2; La, Peiqing2; Ma, Fuliang2; Donic, Tibor1; Wang, Hongding3 | |
刊名 | JOURNAL OF MATERIALS RESEARCH |
2016-06-28 | |
卷号 | 31期号:12页码:1691-1701 |
关键词 | 304 stainless steel aluminothermic reaction thickness reduction microstructures tensile properties |
ISSN号 | 0884-2914 |
DOI | 10.1557/jmr.2016.167 |
英文摘要 | Microstructure evolution and tensile properties of large dimensional bulk 304 stainless steel after being rolled with different thickness reductions were characterized in detail. The results showed that the steel consisted of nano-submicro-microcrystalline austenite and nanocrystalline ferrite. Submicrocrystalline austenite was broken down with the thickness reduction, when thickness reduction was 70%, all submicrocrystalline were broken down to nanocrocrystalline, and dispersed more uniformly in the microcrystalline austenite phase in the steel, but the grain size of the nanocrystalline austenite increased to 70 nm. Tensile strength increased from 850 MPa to 965 MPa, yield strength increased from 652 MPa to 837 MPa, elongation decreased from 33% to 19%, intergranular corrosion rate decreased from 1.36 g/(m(2) h) to 0.46 g/(m(2) h). Strength and intergranular corrosion properties increased much. When the thickness reduction was 70%, the tensile strength, yield strength, elongation, and intergranular corrosion properties were the best in the reported value of the steel. |
资助项目 | National Natural Science Foundation of China[50674051] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | CAMBRIDGE UNIV PRESS |
WOS记录号 | WOS:000379208600006 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/33662] |
专题 | 省部共建有色金属先进加工与再利用国家重点实验室 材料科学与工程学院 |
通讯作者 | La, Peiqing |
作者单位 | 1.Univ Zilina, Fac Mech Engn, Zilina 101026, Slovakia 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Peoples R China 3.Lanzhou Jiaotong Univ, Sch Mechatron Engn, Lanzhou 730070, Peoples R China |
推荐引用方式 GB/T 7714 | Wei, Fuan,La, Peiqing,Ma, Fuliang,et al. Enhanced intergranular corrosion resistance and tensile strength in 304 stainless steel with dispersed nanocrystallines in microcrystalline austenite[J]. JOURNAL OF MATERIALS RESEARCH,2016,31(12):1691-1701. |
APA | Wei, Fuan,La, Peiqing,Ma, Fuliang,Donic, Tibor,&Wang, Hongding.(2016).Enhanced intergranular corrosion resistance and tensile strength in 304 stainless steel with dispersed nanocrystallines in microcrystalline austenite.JOURNAL OF MATERIALS RESEARCH,31(12),1691-1701. |
MLA | Wei, Fuan,et al."Enhanced intergranular corrosion resistance and tensile strength in 304 stainless steel with dispersed nanocrystallines in microcrystalline austenite".JOURNAL OF MATERIALS RESEARCH 31.12(2016):1691-1701. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论