Microstructure and properties of aluminum AA6061-T6 to copper (Cu)-T2 joints by cold metal transfer joining technology | |
Cai, Z. P.1; Ai, B. Q.2; Cao, R.2; Lin, Q.2; Chen, J. H.2 | |
刊名 | JOURNAL OF MATERIALS RESEARCH |
2016-09 | |
卷号 | 31期号:18页码:2876-2887 |
关键词 | Binary alloys Brazing Copper Copper alloys Filler metals Intermetallics Joining Welding Welds Aluminum alloy AA6061 Brazing joints Cold metal transfers Fracture surfaces Joining technology Microstructure and properties Pure copper Stress condition |
ISSN号 | 0884-2914 |
DOI | 10.1557/jmr.2016.295 |
英文摘要 | Recently, cold metal transfer (CMT) process has been successfully applied to weld dissimilar metals. In this paper, two different aluminum alloy AA6061-T6 and pure copper T2 lapped joints were performed by CMT with AA4043 aluminum alloy wire as the filler metal. Results indicated that sound lapped joints between aluminum alloy AA6061-T6 and pure copper T2 could be performed by CMT technology. The joint was composed of Al-Al welding joint and Al-Cu brazing joint. The Al-Al welding joint was formed between the Al weld metal and the Al base metal, and the weld metal in Al-Al welding joint was composed of alpha-Al solid solution, alpha-Al, and CuAl eutectic phase. Al-Cu brazing joint was formed between the Al weld metal and the local molten Cu base metal, and composed of three copper-weld metal interfaces with a large amount of intermetallic compounds (IMCs), i.e., CuAl2, CuAl. The optimum strength of two joints could reach up to 1.23 kN and 1.56 kN, respectively, which was mainly due to the differences of the size of Cu/Al IMCs and stress condition. In addition, the distribution of microhardness and fracture surface of two joints were observed and analyzed in detail. |
资助项目 | National Nature Science Foundation of China[51265028] ; Pre-research of National Basic Research Program of China[2014CB660810] ; Rose Willow Outstanding Individual Programs of Lanzhou University of Technology[J201203] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | CAMBRIDGE UNIV PRESS |
WOS记录号 | WOS:000385675200015 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/33617] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 学报编辑部 |
通讯作者 | Cao, R. |
作者单位 | 1.Tsinghua Univ, Dept Mech Engn, Collaborat Innovat Ctr Adv Nucl Energy Technol, State Key Lab Tribol, Beijing, Peoples R China 2.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou, Peoples R China |
推荐引用方式 GB/T 7714 | Cai, Z. P.,Ai, B. Q.,Cao, R.,et al. Microstructure and properties of aluminum AA6061-T6 to copper (Cu)-T2 joints by cold metal transfer joining technology[J]. JOURNAL OF MATERIALS RESEARCH,2016,31(18):2876-2887. |
APA | Cai, Z. P.,Ai, B. Q.,Cao, R.,Lin, Q.,&Chen, J. H..(2016).Microstructure and properties of aluminum AA6061-T6 to copper (Cu)-T2 joints by cold metal transfer joining technology.JOURNAL OF MATERIALS RESEARCH,31(18),2876-2887. |
MLA | Cai, Z. P.,et al."Microstructure and properties of aluminum AA6061-T6 to copper (Cu)-T2 joints by cold metal transfer joining technology".JOURNAL OF MATERIALS RESEARCH 31.18(2016):2876-2887. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论