Effect and Mechanism of NaCl Content on Phase and Size of Submicron Tungsten Boride Powders by Salt-assisted Combustion Synthesis | |
Han Yijun1; Dong Peng1; La Peiping1; Wei Yupeng1; Guo Xin1; Sheng Jie1; Lan Wei2 | |
刊名 | RARE METAL MATERIALS AND ENGINEERING
![]() |
2018-01 | |
卷号 | 47期号:1页码:131-138 |
关键词 | NaCl content salt-assisted combustion synthesis morphology phase particle size |
ISSN号 | 1002-185X |
英文摘要 | The diluent NaCl was added into the W-B2O3-Mg system to prepare submicron tungsten boride powders via salt-assisted combustion synthesis. The products were analyzed by XRD, SEM and EDS, and the effect of NaCl content on phase composition, morphology and average particle size of the products were studied. Results show that the combustion synthesis products before leaching mainly consist of B2O3 and MgO, and the morphology of particles is similar to ellipsoid when without adding NaCl. After adding NaCl, combustion synthesis products before leaching mainly consist of B2O3, MgO, WB and B, and the morphology of particles is irregular and particles are of slight reunion together. The products after leaching are composed of small sized tungsten boride particles; the average grain size decreases with the increasing of NaCl contents; when the content of NaCl k=20, the smallest particle size is 0.85 mu m. The purity of products after leaching is higher, and the contents of W and B are up to more than 98%. The biggest content value of W and B is 98.51% when the content of NaCl k=5%. |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 中文 |
出版者 | NORTHWEST INST NONFERROUS METAL RESEARCH |
WOS记录号 | WOS:000429187800024 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/32893] ![]() |
专题 | 省部共建有色金属先进加工与再利用国家重点实验室 材料科学与工程学院 石油化工学院 学科建设与学位办公室 |
通讯作者 | La Peiping |
作者单位 | 1.Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China 2.Lanzhou Univ, Lanzhou 730000, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Han Yijun,Dong Peng,La Peiping,et al. Effect and Mechanism of NaCl Content on Phase and Size of Submicron Tungsten Boride Powders by Salt-assisted Combustion Synthesis[J]. RARE METAL MATERIALS AND ENGINEERING,2018,47(1):131-138. |
APA | Han Yijun.,Dong Peng.,La Peiping.,Wei Yupeng.,Guo Xin.,...&Lan Wei.(2018).Effect and Mechanism of NaCl Content on Phase and Size of Submicron Tungsten Boride Powders by Salt-assisted Combustion Synthesis.RARE METAL MATERIALS AND ENGINEERING,47(1),131-138. |
MLA | Han Yijun,et al."Effect and Mechanism of NaCl Content on Phase and Size of Submicron Tungsten Boride Powders by Salt-assisted Combustion Synthesis".RARE METAL MATERIALS AND ENGINEERING 47.1(2018):131-138. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论