The Joining Behavior of Titanium and Q235 Steel Joined by Cold Metal Transfer Joining Technology | |
Chang, Jinghuan; Cao, Rui; Yan, Yingjie | |
刊名 | MATERIALS |
2019-08 | |
卷号 | 12期号:15 |
关键词 | welding-brazing joining mechanism strength dissimilar metal |
DOI | 10.3390/ma12152413 |
英文摘要 | Cold metal transfer process is applied to join titanium and Q235 steel with copper filler metal. Scanning electron microscope (SEM), energy dispersive spectrometer (EDS) analysis, micro-hardness tests, and tensile strength test were performed to investigate the joining mechanism and strength of joints. The results show that the stacking order of two base metals affected the joining modes and strength. For top Q235 steel to bottom Ti-TA2 lapped joint, there was no distinct interface reaction layer between the steel base metal and the weld metal; dispersed TiFe2 intermetalics (IMCs) IMCs between the steel base metal and the Ti base metal greatly improved the strength of joint; the tensile force of the joint could reach up to 93% that of steel-steel joint using the same welding parameters. Additionally, the joints were fractured in dimple mode at the steel base metal. For top Ti-TA2 to bottom Q235 steel lapped joint, the increasing volume fraction of Ti-Cu IMCs at the Ti-Cu weld metal interface contributed to the strength of joint degradation. The joints under tensile loading are initiated at the Ti-Cu weld metal interface between the weld metal and Ti base metal, then propagated to weld metal, finally fractured with brittle mode. |
资助项目 | National Nature Science Foundation of China[51675255][51761027][51265028] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | MDPI |
WOS记录号 | WOS:000482576900074 |
状态 | 已发表 |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.223/handle/2XXMBERH/31654] |
专题 | 材料科学与工程学院 省部共建有色金属先进加工与再利用国家重点实验室 |
通讯作者 | Cao, Rui |
作者单位 | Lanzhou Univ Technol, State Key Lab Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China |
推荐引用方式 GB/T 7714 | Chang, Jinghuan,Cao, Rui,Yan, Yingjie. The Joining Behavior of Titanium and Q235 Steel Joined by Cold Metal Transfer Joining Technology[J]. MATERIALS,2019,12(15). |
APA | Chang, Jinghuan,Cao, Rui,&Yan, Yingjie.(2019).The Joining Behavior of Titanium and Q235 Steel Joined by Cold Metal Transfer Joining Technology.MATERIALS,12(15). |
MLA | Chang, Jinghuan,et al."The Joining Behavior of Titanium and Q235 Steel Joined by Cold Metal Transfer Joining Technology".MATERIALS 12.15(2019). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论