Study on Susceptibility and Mechanism of Reheat Cracking in Welded Joint of Type 347 Austenitic Stainless Steel | |
Wang, Jianjun; Yu, Shurong | |
刊名 | INTERNATIONAL JOURNAL OF CHEMICAL ENGINEERING |
2022-05-31 | |
卷号 | 2022 |
关键词 | Austenitic stainless steelCarbidesCracksGrain boundariesLoad testingScanning electron microscopySpectrum analysisStrain rateWelding Characterization techniquesConstant load testsCracking susceptibilityFracture stressGrain-boundariesHighest temperatureReheat crackingSlow strain rate tensile testSteel welded jointsTemperature constant |
ISSN号 | 1687-806X |
DOI | 10.1155/2022/2016388 |
英文摘要 | The reheat cracking susceptibility of welded joints has been evaluated by 900 degrees C high-temperature constant load test and 750 degrees C-900 degrees C high-temperature slow strain rate tensile (SSRT) test on welded joints of TP347 steel, and the influencing factors and mechanism of reheat cracking in welded joints have been further investigated by microcosmic characterization techniques of SEM and EDS, etc. The result shows the critical fracture stress of TP347 steel welded joints at 900 degrees C is 24 MPa, which is much lower than 80% of the high-temperature yield strength of base material, indicating that the reheat crack of the welded joint is highly sensitive at this temperature; the average reduction of area (RoA) of welded joints obtained by 750 degrees C-900 degrees C SSRT test at each temperature is below 20%, which means all welded joints have a reheat cracking susceptibility in this temperature range, and the reheat cracking susceptibility increases with the rising of temperature. Based on study and analysis using microcosmic methods of optical microscope, scanning electron microscope, and energy spectrum analysis, it is found that welded joints of TP347 steel have a high reheat cracking susceptibility because the high temperature accelerates the diffusion of Cr, Nb, and impurity elements to the grain boundary, and a large quantity of carbides and low-melting-point eutectics are collected and precipitated at the grain boundary to reduce the plasticity of the grain boundary. Since there is a high welding residual stress in welded joints, cavities are formed under the action of the stress at a high temperature, and the merging of cavities causes the formation of cracks which extend along the grain boundary. |
WOS研究方向 | Engineering |
语种 | 英语 |
出版者 | HINDAWI LTD |
WOS记录号 | WOS:000810918300001 |
内容类型 | 期刊论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/158845] |
专题 | 兰州理工大学 |
作者单位 | Lanzhou Univ Technol, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Jianjun,Yu, Shurong. Study on Susceptibility and Mechanism of Reheat Cracking in Welded Joint of Type 347 Austenitic Stainless Steel[J]. INTERNATIONAL JOURNAL OF CHEMICAL ENGINEERING,2022,2022. |
APA | Wang, Jianjun,&Yu, Shurong.(2022).Study on Susceptibility and Mechanism of Reheat Cracking in Welded Joint of Type 347 Austenitic Stainless Steel.INTERNATIONAL JOURNAL OF CHEMICAL ENGINEERING,2022. |
MLA | Wang, Jianjun,et al."Study on Susceptibility and Mechanism of Reheat Cracking in Welded Joint of Type 347 Austenitic Stainless Steel".INTERNATIONAL JOURNAL OF CHEMICAL ENGINEERING 2022(2022). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论