Research on fabrication and semisolid processing of semisolid slurries of 7075 aluminum matrix composites reinforced with Nano-sized SiC particles | |
Jiang, Ju Fu1,2; Wang, Ying3; Luo, Shou Jing1 | |
2016 | |
会议日期 | October 23, 2016 - October 27, 2016 |
会议地点 | Salt Lake City, UT, United states |
关键词 | Aluminum Aluminum alloys Fabrication Mechanical properties Microstructure Reinforcement Silicon carbide Silicon compounds Tensile strength Wear resistance Aluminum matrix composites Cylindrical composites Dislocation densities Reinforcement particles Rheo forming SiC particles Thixo-forming Ultimate tensile strength |
卷号 | 256 |
DOI | 10.4028/www.scientific.net/SSP.256.81 |
页码 | 81-87 |
英文摘要 | Semisolid slurries of 7075 aluminum matrix composite reinforced with nano-sized SiC particles were fabricated by ultrasonic assisted semisolid stirring (UASS) method. Rheoforming and thixoforming of typical cylindrical parts were investigated. The results show that high-quality semisolid slurries with spheroidal solid grain of 38 μm were fabricated by UASS. The nano-sized SiC particles were dispersed uniformly due to transient cavitation and acoustic streaming of ultrasonic wave and high and controllable viscosity of semisolid slurry. Typical cylindrical composite parts with good surface quality and complete filling were rheoformed and thixoformed successfully. Ultimate tensile strength (UTS) of the rheoformed and thixoformed composite parts are enhanced due to addition of nano-sized SiC particles. However, elongation decreased as compared to those of the matrix parts. Maximum UTS of 550 MPa was achieved in the thixoformed composite part with T6 treatment. Increase of dislocation density around the reinforcement particles leads to improvement of the strength and wear resistance of the composite. © 2016 Trans Tech Publications, Switzerland. |
会议录 | Solid State Phenomena |
会议录出版者 | Trans Tech Publications Ltd |
语种 | 英语 |
ISSN号 | 10120394 |
内容类型 | 会议论文 |
源URL | [http://ir.lut.edu.cn/handle/2XXMBERH/117446] |
专题 | 兰州理工大学 材料科学与工程学院 |
作者单位 | 1.School of Materials Science and Engineering, Harbin Institute of Technology, Harbin; 150001, China; 2.State Key Laboratory of Advanced Processing and Recycling of Non-ferrous Metals, Lanzhou University of Technology, Lanzhou; 730050, China; 3.School of Mechatronics Engineering, Harbin Institute of Technology, Harbin; 150001, China |
推荐引用方式 GB/T 7714 | Jiang, Ju Fu,Wang, Ying,Luo, Shou Jing. Research on fabrication and semisolid processing of semisolid slurries of 7075 aluminum matrix composites reinforced with Nano-sized SiC particles[C]. 见:. Salt Lake City, UT, United states. October 23, 2016 - October 27, 2016. |