Hydrogen Permeation Behavior of Carbon Steel During Corrosion in Highly Pressed Saturated Bentonite | |
Zhang, Qichao1,2; Jiang, Yishan1; Zhao, Xin1; Song, Penglei1; Kuang, Tingting2; Chen, Juna1; Sun, Zhongtao1; Zhang, Yaopeng1; Ai, Xiayu1; Lu, Dongzhu2 | |
刊名 | FRONTIERS IN MATERIALS |
2022-03-21 | |
卷号 | 9页码:11 |
关键词 | hydrogen embrittlement metal corrosion hydrogen permeation bentonite nuclear waste |
ISSN号 | 2296-8016 |
DOI | 10.3389/fmats.2022.848123 |
通讯作者 | Lu, Dongzhu(421241006@qq.com) ; Huang, Yanliang(263342066@qq.com) |
英文摘要 | Deep geological disposal is the most reliable method for high-level nuclear waste, of which metal container as the first barrier for deep geological disposal of high-level nuclear waste is particularly important. Carbon steel is used as a container material because of the low possibility of local corrosion in bentonite. However, after the storage is closed, the decrease of oxygen content will create a near-field environment where the hydrogen embrittlement (HE) in the corrosion process of the container could happen. To evaluate the safety of containers in deep geological disposal of Beshai, the preselected area in China, hydrogen permeation efficiency and HE were estimated in highly pressed saturated bentonite by electrochemical and extrapolation analyses. It is concluded that hydrogen permeation efficiency increases with the disposal year, which proves that the hydrogen evolution reaction dominates the cathode process in the corrosion during long-term disposal. However, slow strain rate tensile shows that Q235 steel has a low HE sensitivity. |
资助项目 | National Natural Science Foundation of China[51471160] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | FRONTIERS MEDIA SA |
WOS记录号 | WOS:000779125000001 |
内容类型 | 期刊论文 |
源URL | [http://ir.qdio.ac.cn/handle/337002/178837] |
专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
通讯作者 | Lu, Dongzhu; Huang, Yanliang |
作者单位 | 1.Navy Submarine Acad, Qingdao, Peoples R China 2.Chinese Acad Sci, Inst Oceanol, CAS Key Lab Marine Environm Corros & Biofouling, Qingdao, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Qichao,Jiang, Yishan,Zhao, Xin,et al. Hydrogen Permeation Behavior of Carbon Steel During Corrosion in Highly Pressed Saturated Bentonite[J]. FRONTIERS IN MATERIALS,2022,9:11. |
APA | Zhang, Qichao.,Jiang, Yishan.,Zhao, Xin.,Song, Penglei.,Kuang, Tingting.,...&Huang, Yanliang.(2022).Hydrogen Permeation Behavior of Carbon Steel During Corrosion in Highly Pressed Saturated Bentonite.FRONTIERS IN MATERIALS,9,11. |
MLA | Zhang, Qichao,et al."Hydrogen Permeation Behavior of Carbon Steel During Corrosion in Highly Pressed Saturated Bentonite".FRONTIERS IN MATERIALS 9(2022):11. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论