Microstructural evolution and stress relaxation cracking mechanism for Super304H austenitic stainless steel weld metal | |
Xiao, Xiaopeng1,2; Li, Dianzhong1; Li, Yiyi1,3; Lu, Shanping1 | |
刊名 | JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY |
2022-02-20 | |
卷号 | 100页码:82-90 |
关键词 | Stress relaxation cracking Super304H steel Weld metal Aging treatment Residual stress Precipitates |
ISSN号 | 1005-0302 |
DOI | 10.1016/j.jmst.2021.06.010 |
通讯作者 | Lu, Shanping(shplu@imr.ac.cn) |
英文摘要 | The pre-compressed CT technique was used to quantitatively investigate the formation of stress relaxation cracks under different tensile residual stresses and aging time in Super304H austenitic stainless steel weld metal. The statistical results revealed that intergranular cracks could occur within 2000 h under 650 degrees C when the residual stress was applied with greater than 18 KN pre-compression force. Detailed grain interior and boundary analyses showed that the growth of intragranular Cu-rich particles could induce a strong grain interior, and the intergranular Nb(C, N) carbides were one of the causes to crack under short-term aging time. For long-term aging time conditions, the intergranular M23C6 carbides were more susceptible to crack than intergranular Nb(C, N) carbides. Finally, the mechanism responsible for stress relaxation cracking formation was carefully illustrated for the weld metals after short-term aging and long-term aging, respectively. (C) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology. |
资助项目 | Shenyang National Laboratory for Materials Science Innovation Projects[L2019R35] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | JOURNAL MATER SCI TECHNOL |
WOS记录号 | WOS:000743264400011 |
资助机构 | Shenyang National Laboratory for Materials Science Innovation Projects |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/173296] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Lu, Shanping |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 2.Univ Sci & Technol China, Sch Mat Sci & Engn, Shenyang 110016, Peoples R China 3.Chinese Acad Sci, Insititute Met Res, Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Xiao, Xiaopeng,Li, Dianzhong,Li, Yiyi,et al. Microstructural evolution and stress relaxation cracking mechanism for Super304H austenitic stainless steel weld metal[J]. JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,2022,100:82-90. |
APA | Xiao, Xiaopeng,Li, Dianzhong,Li, Yiyi,&Lu, Shanping.(2022).Microstructural evolution and stress relaxation cracking mechanism for Super304H austenitic stainless steel weld metal.JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY,100,82-90. |
MLA | Xiao, Xiaopeng,et al."Microstructural evolution and stress relaxation cracking mechanism for Super304H austenitic stainless steel weld metal".JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY 100(2022):82-90. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论