Microstructure Refinement on Crevice Corrosion of High-Speed Rail Steel U75V Visualized by an In Situ Monitoring System | |
Wang, Jian2,3,4; Zhang, Binbin1,3,4; Xu, Weichen1,3,4; Zhang, Jie1,3,4; Yang, Lihui1,3,4; Peng, Zhongbo2; Hou, Baorong1,3,4 | |
刊名 | FRONTIERS IN MATERIALS |
2022-01-07 | |
卷号 | 8页码:12 |
关键词 | microstructure crevice corrosion pearlite cooling rate U75V rail steel interlamellar spacing |
ISSN号 | 2296-8016 |
DOI | 10.3389/fmats.2021.820721 |
通讯作者 | Xu, Weichen(w.xu@qdio.ac.cn) ; Zhang, Jie(zhangjie@qdio.ac.cn) |
英文摘要 | Rail foot covered by a fastener will suffer from crevice corrosion, leading to thinning and localized attack of crevice interior posing a risk of failure. This work investigated crevice corrosion behavior of a typical pearlitic high-speed rail steel U75V, focusing for the first time on the effect of pearlitic microstructure refinement achieved by heat treatment with different cooling rates 2, 5, and 10 degrees C/s. Under anodic polarization, localized dissolved spots presented on the as-received sample, where crevice corrosion mostly initiated from. For cooling rates 2 and 5 degrees C/s, localized dissolved spots were also observed but crevice corrosion was mostly presented as general corrosion instead of from local spots, ascribed to enhanced tendency of uniform dissolution due to microstructure refinement and homogenization. For cooling rate 10 degrees C/s, crevice corrosion expanded flocculently, ascribed to preferential dissolution of pearlitic nodules with entangled cementite due to over refinement. Crevice corrosion was obviously accelerated by microstructure refinement. Cooling rates 5 and 10 degrees C/s led to the fastest and slowest expansion of the corroded area, respectively, while the corrosion depth was just the opposite based on the same amount of metal loss. This work provides important information regarding the effect of pearlitic microstructure refinement on crevice corrosion and introduces a facile method for in situ monitoring of crevice corrosion. |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | FRONTIERS MEDIA SA |
WOS记录号 | WOS:000756964300001 |
内容类型 | 期刊论文 |
源URL | [http://ir.qdio.ac.cn/handle/337002/178014] |
专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
通讯作者 | Xu, Weichen; Zhang, Jie |
作者单位 | 1.Chinese Acad Sci, Ctr Ocean Mega Sci, Qingdao, Peoples R China 2.Chongqing Jiaotong Univ, Sch Shipping & Naval Architecture, Chongqing, Peoples R China 3.Pilot Natl Lab Marine Sci & Technol Qingdao, Open Studio Marine Corros & Protect, Qingdao, Peoples R China 4.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Jian,Zhang, Binbin,Xu, Weichen,et al. Microstructure Refinement on Crevice Corrosion of High-Speed Rail Steel U75V Visualized by an In Situ Monitoring System[J]. FRONTIERS IN MATERIALS,2022,8:12. |
APA | Wang, Jian.,Zhang, Binbin.,Xu, Weichen.,Zhang, Jie.,Yang, Lihui.,...&Hou, Baorong.(2022).Microstructure Refinement on Crevice Corrosion of High-Speed Rail Steel U75V Visualized by an In Situ Monitoring System.FRONTIERS IN MATERIALS,8,12. |
MLA | Wang, Jian,et al."Microstructure Refinement on Crevice Corrosion of High-Speed Rail Steel U75V Visualized by an In Situ Monitoring System".FRONTIERS IN MATERIALS 8(2022):12. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论