Preparation of Syringaldehyde from Lignin by Catalytic Oxidation of Perovskite-Type Oxides | |
Li, Ying-xia2; Zhu, Jun-peng1,2; Zhang, Zhong-jun1,2; Qu, Yong-Shui1 | |
刊名 | ACS OMEGA |
2020-02-11 | |
卷号 | 5期号:5页码:2107-2113 |
ISSN号 | 2470-1343 |
DOI | 10.1021/acsomega.9b02379 |
英文摘要 | The influence of different reaction conditions on the yield of syringaldehyde was studied by using perovskite oxide as the catalyst. The optimal reaction conditions are as follows: 0.60 g of dealkali lignin, 0.60 g of 5 wt % theta ring-loaded LaFe0.2Cu0.8O3 catalyst, 30 mL of 1.0 mol/L NaOH solution, 160 degrees C reaction temperature, 0.80 MPa O-2 pressure, and 2.5 h reaction time. Under these conditions, the highest syringaldehyde yield was 10.00%. The recycling performance of the catalyst was studied. It was found by XRD analysis that the catalyst maintained high catalytic activity after four times of use. |
资助项目 | National Natural Science Foundation of China[21706263] |
WOS关键词 | CU ; DEGRADATION ; EXTRACTION ; SULFUR ; OXYGEN ; ALLOY ; CO |
WOS研究方向 | Chemistry |
语种 | 英语 |
出版者 | AMER CHEMICAL SOC |
WOS记录号 | WOS:000513942200008 |
资助机构 | National Natural Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.ipe.ac.cn/handle/122111/39612] |
专题 | 中国科学院过程工程研究所 |
通讯作者 | Qu, Yong-Shui |
作者单位 | 1.Chinese Acad Sci, State Key Lab Biochem Engn, Inst Proc Engn, Beijing 100190, Peoples R China 2.Beijing Univ Chem Technol, Beijing 100029, Peoples R China |
推荐引用方式 GB/T 7714 | Li, Ying-xia,Zhu, Jun-peng,Zhang, Zhong-jun,et al. Preparation of Syringaldehyde from Lignin by Catalytic Oxidation of Perovskite-Type Oxides[J]. ACS OMEGA,2020,5(5):2107-2113. |
APA | Li, Ying-xia,Zhu, Jun-peng,Zhang, Zhong-jun,&Qu, Yong-Shui.(2020).Preparation of Syringaldehyde from Lignin by Catalytic Oxidation of Perovskite-Type Oxides.ACS OMEGA,5(5),2107-2113. |
MLA | Li, Ying-xia,et al."Preparation of Syringaldehyde from Lignin by Catalytic Oxidation of Perovskite-Type Oxides".ACS OMEGA 5.5(2020):2107-2113. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论