Irradiation response of Al2O3-ZrO2 ceramic composite under He ion irradiation | |
Liu, Yiwen; Zhu, Yabin; Shen, Tielong; Chai, Jianlong; Niu, Lijuan; Li, Shufen; Jin, Peng; Zheng, Hai; Wang, Zhiguang | |
刊名 | JOURNAL OF THE EUROPEAN CERAMIC SOCIETY |
2021-04-01 | |
卷号 | 41期号:4页码:2883-2891 |
关键词 | He ion Irradiation damage Mechanical properties |
ISSN号 | 0955-2219 |
DOI | 10.1016/j.jeurceramsoc.2020.11.042 |
通讯作者 | Zhu, Yabin(zhuyabin@impcas.ac.cn) ; Wang, Zhiguang(zhgwang@impcas.ac.cn) |
英文摘要 | The dense Al2O3-ZrO2 ceramic composite prepared by spark plasma sintering was irradiated by 500 keV He ions with different fluences and temperatures. The microstructural evolution and mechanical properties were investigated. The results showed that peak broadening and shifts at RT revealed by GIXRD and Raman are associated with damage induced microstrain and formation of point defects. The recovery at 500 degrees C suggested the reduction of irradiation induced damage. Compared with alpha-Al2O3, t-ZrO2 exhibited a reverse trend in lattice parameters change and lattice expansion. Many helium bubbles with oblate and ribbon-like shape were mainly formed in alpha-Al2O3 grains at He concentration peak at 1.0 x 10(17) ions/cm(2). With increasing of fluence at RT, ribbon-like helium bubbles developed into microcracks at 4.0 x 1017 ions/cm(2). Though evident structural changes, no full amorphization was observed at 4.0 x 10(17) ions/cm(2). Formation of ribbon-like bubbles and microcracks is the main mechanism for degradation of mechanical properties of irradiated Al2O3-ZrO2 composite. |
资助项目 | National Natural Science Foundation of China[U1832206] ; National Natural Science Foundation of China[11805245] ; National Natural Science Foundation of China[11505247] ; National Natural Science Foundation of China[U1832149] ; Strategic Priority Research Program of the Chinese Academy of Sciences[XDA21010202] ; Sichuan Province Science and Technology Program[2018JZ0014] ; National Key Research and Development Project[2018YFE0307100] ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology)[ZDRW-CN-2017-1] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000613766900005 |
资助机构 | National Natural Science Foundation of China ; Strategic Priority Research Program of the Chinese Academy of Sciences ; Sichuan Province Science and Technology Program ; National Key Research and Development Project ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology) |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.186/handle/113462/138017] |
专题 | 中国科学院近代物理研究所 |
通讯作者 | Zhu, Yabin; Wang, Zhiguang |
作者单位 | Chinese Acad Sci, Inst Modern Phys, Lanzhou 730000, Peoples R China |
推荐引用方式 GB/T 7714 | Liu, Yiwen,Zhu, Yabin,Shen, Tielong,et al. Irradiation response of Al2O3-ZrO2 ceramic composite under He ion irradiation[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,2021,41(4):2883-2891. |
APA | Liu, Yiwen.,Zhu, Yabin.,Shen, Tielong.,Chai, Jianlong.,Niu, Lijuan.,...&Wang, Zhiguang.(2021).Irradiation response of Al2O3-ZrO2 ceramic composite under He ion irradiation.JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,41(4),2883-2891. |
MLA | Liu, Yiwen,et al."Irradiation response of Al2O3-ZrO2 ceramic composite under He ion irradiation".JOURNAL OF THE EUROPEAN CERAMIC SOCIETY 41.4(2021):2883-2891. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论