Enhancing strengthening efficiency of graphene nano-sheets in aluminum matrix composite by improving interface bonding | |
Liu, Z. Y.2; Wang, L. H.2; Zan, Y. N.2; Wang, W. G.1; Xiao, B. L.2; Wang, D.2; Wang, Q. Z.2; Ni, D. R.2; Ma, Z. Y.2 | |
刊名 | COMPOSITES PART B-ENGINEERING |
2020-10-15 | |
卷号 | 199页码:11 |
关键词 | Metal-matrix composites Interface Mechanical properties Strength |
ISSN号 | 1359-8368 |
DOI | 10.1016/j.compositesb.2020.108268 |
通讯作者 | Xiao, B. L.(blxiao@imr.ac.cn) ; Ma, Z. Y.(zyma@imr.ac.cn) |
英文摘要 | Three 0.3 vol% graphene nano-sheet reinforced Al composites (GNS/Al), namely forged GNS/Al-4Cu, extruded GNS/Al-4Cu and forged GNS/Al-4Cu-1Mg, with different graphene-Al interfaces were prepared by wet mixing of graphene oxide aqueous solution and flaky Al powders, thermal reduction and subsequent powder metallurgy route. Their strengthening behaviors related with interface bonding were investigated, with the help of high resolution transmission electron microscopy, X-ray photoelectron spectroscopy and interface bonding test of specially designed model materials. In the forged composite, amorphous Al2O3 layer was observed between GNS and Al, resulting in a weak bonding of GNS and Al with interface shear strength of 117 MPa and normal strength of 227 MPa. In this case, nearly no strengthening effect was achieved by GNS addition. Using extruding to replace forging or adding Mg element could respectively break or exhaust amorphous Al2O3 layers, leading to improved graphene-Al interface bonding strength due to high fraction of Al-C ionic bond, thereby significantly increasing the strengthening effect of GNS. The best strengthening efficiency with a strengthening factor of similar to 33 was achieved in the forged GNS/Al-4Cu-1Mg due to strong interface shear strength of 209 MPa and normal strength of 402 MPa. |
资助项目 | National Key R&D Program of China[2017YFB0703104] ; Key Research Program of Frontier Sciences, CAS[QYZDJ-SSW-JSC015] ; National Natural Science Foundation of China[51501189] ; Youth Innovation Promotion Association CAS[2020197] |
WOS研究方向 | Engineering ; Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000571760800004 |
资助机构 | National Key R&D Program of China ; Key Research Program of Frontier Sciences, CAS ; National Natural Science Foundation of China ; Youth Innovation Promotion Association CAS |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/140567] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Xiao, B. L.; Ma, Z. Y. |
作者单位 | 1.Liaoning Shihua Univ, 1 Dandong Rd, Fushun 113001, Peoples R China 2.Chinese Acad Sci, Inst Met Res, 72 Wenhua Rd, Shenyang 110016, Peoples R China |
推荐引用方式 GB/T 7714 | Liu, Z. Y.,Wang, L. H.,Zan, Y. N.,et al. Enhancing strengthening efficiency of graphene nano-sheets in aluminum matrix composite by improving interface bonding[J]. COMPOSITES PART B-ENGINEERING,2020,199:11. |
APA | Liu, Z. Y..,Wang, L. H..,Zan, Y. N..,Wang, W. G..,Xiao, B. L..,...&Ma, Z. Y..(2020).Enhancing strengthening efficiency of graphene nano-sheets in aluminum matrix composite by improving interface bonding.COMPOSITES PART B-ENGINEERING,199,11. |
MLA | Liu, Z. Y.,et al."Enhancing strengthening efficiency of graphene nano-sheets in aluminum matrix composite by improving interface bonding".COMPOSITES PART B-ENGINEERING 199(2020):11. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论