In-situ reaction synthesis and mechanical properties of quaternary MAX phase (Cr2/3Ti1/3)(3)AlC2 | |
Liu, Zhimou1; Yang, Jia2; Qian, Yuhai1; Xu, Jingjun1; Zuo, Jun1; Li, Meishuan1 | |
刊名 | CERAMICS INTERNATIONAL |
2020-10-01 | |
卷号 | 46期号:14页码:22854-22860 |
关键词 | Quaternary MAX Phase (Cr2/3Ti1/3)(3)AlC2 Reaction route Mechanical property |
ISSN号 | 0272-8842 |
DOI | 10.1016/j.ceramint.2020.06.055 |
通讯作者 | Qian, Yuhai(yhqian@imr.ac.cn) ; Li, Meishuan(mshli@imr.ac.cn) |
英文摘要 | Bulk quaternary MAX phase (Cr2/3Ti1/3)(3)AlC2 was synthesized by in-situ reaction/hot pressing method using Cr, Ti, Al, and C powders as starting materials. The involved reaction routes during hot-pressing were determined according to XRD and SEM/EDS analysis results. The possible chemical reactions involved during hot pressing process were proposed. It was revealed that the desired (Cr2/3Ti1/3)(3)AlC2 was formed via the reaction between intermediate products of ternary MAX Cr2AlC and carbide TiC, providing another path for the preparation of high order MAX phase. Tests of mechanical properties suggested that the Vickers hardness of (Cr2/3Ti1/3)(3)AlC2 was 5.6 GPa, higher than that of the ternary MAX phase Ti3AlC2. Its flexural and compressive strength were determined to be 493 MPa and 1407 MPa at room temperature, respectively. Flexural strength maintained a relatively high level of 424 MPa up to 1000 degrees C, about 90% of that at room temperature. The dependence of elastic modulus on increasing temperatures exhibited similar tendency to that of flexural strength. The as-synthesized (Cr2/3Ti1/3)(3)AlC2, a unique quaternary layered nano-laminated carbide, was a promising high temperature structural material with its attractively comprehensive properties. |
资助项目 | National Natural Science Foundation of China, China[51271191] ; National Natural Science Foundation of China, China[51571205] |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000558707400110 |
资助机构 | National Natural Science Foundation of China, China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/140252] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Qian, Yuhai; Li, Meishuan |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, 72 Wenhua Rd, Shenyang 110016, Peoples R China 2.Hunan Univ Technol, Sch Mech Engn, Zhuzhou 412007, Peoples R China |
推荐引用方式 GB/T 7714 | Liu, Zhimou,Yang, Jia,Qian, Yuhai,et al. In-situ reaction synthesis and mechanical properties of quaternary MAX phase (Cr2/3Ti1/3)(3)AlC2[J]. CERAMICS INTERNATIONAL,2020,46(14):22854-22860. |
APA | Liu, Zhimou,Yang, Jia,Qian, Yuhai,Xu, Jingjun,Zuo, Jun,&Li, Meishuan.(2020).In-situ reaction synthesis and mechanical properties of quaternary MAX phase (Cr2/3Ti1/3)(3)AlC2.CERAMICS INTERNATIONAL,46(14),22854-22860. |
MLA | Liu, Zhimou,et al."In-situ reaction synthesis and mechanical properties of quaternary MAX phase (Cr2/3Ti1/3)(3)AlC2".CERAMICS INTERNATIONAL 46.14(2020):22854-22860. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论