Microstructures and high-temperature mechanical properties of a directionally solidified Ni-based superalloy: Influence of boron content
Zhang, H. W.1,2; Wu, Y. S.2; Qin, X. Z.2; Zhou, L. Z.2; Li, X. W.1
刊名JOURNAL OF ALLOYS AND COMPOUNDS
2018-10-30
卷号767页码:915-923
关键词Directionally solidified Ni-based superalloy Boron Microstructure High-temperature tension Stress rupture
ISSN号0925-8388
DOI10.1016/j.jallcom.2018.07.162
通讯作者Qin, X. Z.(xzqin@imr.ac.cn) ; Li, X. W.(xwli@mail.neu.edu.cn)
英文摘要The effects of boron content on the microstructure and mechanical properties of a directionally solidified Ni-based superalloy were investigated. The increase of boron content significantly increases the amount of gamma/gamma' eutectic, impels the formation of multi-phase eutectic-like constituent, and promotes the morphological transformation of MC carbides from rod-like to blocky. After standard heat treatment, the incipient melting occurs in the high boron alloy, which can lower the dissolving temperature of gamma/gamma' eutectic. With increasing boron content, the volume fraction of secondary gamma' phase decreases significantly and the homogeneity and alignment of secondary gamma' show a decrease, and the tensile strengths at 900 degrees C decrease slightly mainly due to the strengthening effect of much more tertiary gamma' phases. The wide gamma matrix channel facilitates the movement of dislocations, which is somewhat beneficial to the elongation, while the incipiently melted region (IMR), the decreased volume fraction of secondary gamma' phase and the less homogeneity of secondary gamma' phase are rather harmful to the elongation. Consequently, the elongation is drastically reduced. The existence of a large amount of IMRs is principally responsible for the reduction of the stress rupture property. Tertiary gamma' phases re-dissolving in g matrix channel facilitates the movement of dislocations between large secondary gamma' phases, which is beneficial to the elongation of the alloys. In addition, the IMRs provide masses of crack sources, and consume the precipitation strengthening elements (Ti, Ta) and the solid solution strengthening elements (Cr, Wand Mo), which plays the major role in the degradation of the high-temperature tensile or stress rupture properties. (C) 2018 Elsevier B.V. All rights reserved.
资助项目National Natural Science Foundation of China (NSFC)[51571058] ; National Natural Science Foundation of China (NSFC)[51001101] ; National High-tech RD Program[2012AA03A501] ; Open Foundation of Key Laboratory for Anisotropy and Texture of Materials, Ministry of Education, Northeastern University, China[ATM20170001]
WOS研究方向Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering
语种英语
出版者ELSEVIER SCIENCE SA
WOS记录号WOS:000446316500110
资助机构National Natural Science Foundation of China (NSFC) ; National High-tech RD Program ; Open Foundation of Key Laboratory for Anisotropy and Texture of Materials, Ministry of Education, Northeastern University, China
内容类型期刊论文
源URL[http://ir.imr.ac.cn/handle/321006/129898]  
专题金属研究所_中国科学院金属研究所
通讯作者Qin, X. Z.; Li, X. W.
作者单位1.Northeastern Univ, Dept Mat Phys & Chem, Sch Mat Sci & Engn, Key Lab Anisotropy & Texture Mat,Minist Educ, Shenyang 110819, Liaoning, Peoples R China
2.Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China
推荐引用方式
GB/T 7714
Zhang, H. W.,Wu, Y. S.,Qin, X. Z.,et al. Microstructures and high-temperature mechanical properties of a directionally solidified Ni-based superalloy: Influence of boron content[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2018,767:915-923.
APA Zhang, H. W.,Wu, Y. S.,Qin, X. Z.,Zhou, L. Z.,&Li, X. W..(2018).Microstructures and high-temperature mechanical properties of a directionally solidified Ni-based superalloy: Influence of boron content.JOURNAL OF ALLOYS AND COMPOUNDS,767,915-923.
MLA Zhang, H. W.,et al."Microstructures and high-temperature mechanical properties of a directionally solidified Ni-based superalloy: Influence of boron content".JOURNAL OF ALLOYS AND COMPOUNDS 767(2018):915-923.
个性服务
查看访问统计
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。


©版权所有 ©2017 CSpace - Powered by CSpace