Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water

doi:10.1016/j.corsci.2018.07.010

CORC > 金属研究所 > 中国科学院金属研究所

	Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water
	Liao, Jiapeng 1,3; Tan, Jibo 1; Wu, Xinqiang 1; Tang, Lichen 2; Qian, Hao 2; Xie, Yongcheng 2
刊名	CORROSION SCIENCE
	2018-08-15
卷号	141 页码:158-167
关键词	Alloy SEM Fretting corrosion Corrosion fatigue High-temperature corrosion
ISSN号	0010-938X
DOI	10.1016/j.corsci.2018.07.010
通讯作者	Wu, Xinqiang(xqwu@imr.ac.cn)
英文摘要	Fretting corrosion fatigue behaviour of Alloy 690 was investigated in 285 degrees C pure water under different normal loads. With increasing the normal load applied, the fatigue life decreased, more severe surface damage and subsurface deformation were observed. The effects of normal loads on crack characteristics on the longitudinal sections across the fretting fatigue scars and corrosion fatigue fractures were examined. Possible influence of the normal loads on initiation and propagation mechanisms of the fretting corrosion fatigue cracks of Alloy 690 in high-temperature pure water are discussed.
资助项目	National Science and Technology Major Project[2017ZX06002003-004-002] ; National Natural Science Foundation of China[51671201] ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology)[ZDRW-CN-2017-1] ; Innovation Fund of Institute of Metal Research, Chinese Academy of Sciences[SCJJ-2013-ZD-02]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	PERGAMON-ELSEVIER SCIENCE LTD
WOS记录号	WOS:000441682000017
资助机构	National Science and Technology Major Project ; National Natural Science Foundation of China ; Key Programs of the Chinese Academy of Sciences (Research on the Development of Nuclear Power Materials and Service Security Technology) ; Innovation Fund of Institute of Metal Research, Chinese Academy of Sciences
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/129063]
专题	金属研究所_中国科学院金属研究所
通讯作者	Wu, Xinqiang
作者单位	1.Chinese Acad Sci, Inst Met Res, Liaoning Key Lab Safety & Assessment Tech Nucl Ma, CAS Key Lab Nucl Mat & Safety Assessment, Shenyang 110016, Liaoning, Peoples R China 2.Shanghai Nucl Engn Res & Design Inst, Shanghai 200233, Peoples R China 3.Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Anhui, Peoples R China
推荐引用方式 GB/T 7714	Liao, Jiapeng,Tan, Jibo,Wu, Xinqiang,et al. Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water[J]. CORROSION SCIENCE,2018,141:158-167.
APA	Liao, Jiapeng,Tan, Jibo,Wu, Xinqiang,Tang, Lichen,Qian, Hao,&Xie, Yongcheng.(2018).Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water.CORROSION SCIENCE,141,158-167.
MLA	Liao, Jiapeng,et al."Effects of normal load on fretting corrosion fatigue of Alloy 690 in 285 degrees C pure water".CORROSION SCIENCE 141(2018):158-167.