INHIBITION EFFECTS OF I- AND I2 ON STRESS-CORROSION CRACKING OF STAINLESS-STEEL IN ACIDIC CHLORIDE SOLUTIONS | |
HUANG, YL; CAO, CN; LU, M; LIN, HC | |
刊名 | CORROSION
![]() |
1993-08-01 | |
卷号 | 49期号:8页码:644-649 |
关键词 | CHLORIDE INHIBITOR STAINLESS STEEL STRESS CORROSION CRACKING |
ISSN号 | 0010-9312 |
通讯作者 | HUANG, YL() |
英文摘要 | Stress corrosion cracking (SCC) of AISI 321 (UNS S32100) stainless steel (SS) in 0.5 mol/L sodium chloride (NaCl) + 0.5 mol/L hydrochloric acid (HCI) solution and the inhibition effects of some iodides and iodine (I2) were studied using the slow strain rate technique. Iodides studied were tetramethyl ammonium iodide (TMAI), tetrabutyl ammonium iodide (TBAI) and potassium iodide (KI). The additives effectively inhibited SCC of AISI 321 in the solution. Inhibition effects resulted mainly from the role of iodide ion. Electrochemical measurements showed the corrosion current density (I(corr)) of the steel increased rapidly and then fluctuated as strain increased. The increase in I(corr) was markedly slower in solutions containing I- ions or I2. Inhibition effects of I- ions and I2 on SCC were attributed to the anodic reaction of the corrosion process and reduction of the accelerating effect of strain on I(corr). |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | NATL ASSN CORROSION ENG |
WOS记录号 | WOS:A1993LU76700004 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/125994] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | HUANG, YL |
作者单位 | CHINESE ACAD SCI,INST CORROS & PROTECT MET,CORROS SCI LAB,SHENYANG 110015,PEOPLES R CHINA |
推荐引用方式 GB/T 7714 | HUANG, YL,CAO, CN,LU, M,et al. INHIBITION EFFECTS OF I- AND I2 ON STRESS-CORROSION CRACKING OF STAINLESS-STEEL IN ACIDIC CHLORIDE SOLUTIONS[J]. CORROSION,1993,49(8):644-649. |
APA | HUANG, YL,CAO, CN,LU, M,&LIN, HC.(1993).INHIBITION EFFECTS OF I- AND I2 ON STRESS-CORROSION CRACKING OF STAINLESS-STEEL IN ACIDIC CHLORIDE SOLUTIONS.CORROSION,49(8),644-649. |
MLA | HUANG, YL,et al."INHIBITION EFFECTS OF I- AND I2 ON STRESS-CORROSION CRACKING OF STAINLESS-STEEL IN ACIDIC CHLORIDE SOLUTIONS".CORROSION 49.8(1993):644-649. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论