Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite

CORC > 金属研究所 > 中国科学院金属研究所

	Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite
	Guo, JT; Cui, CY; Chen, YX; Li, DX; Ye, HQ
刊名	INTERMETALLICS
	2001-04-01
卷号	9 期号:4 页码:287-297
关键词	nickel aluminides based on NiAl brittleness and ductility mechanical properties at high temperatures hot isostatic dressing microstructure
ISSN号	0966-9795
通讯作者	Guo, JT()
英文摘要	A NiAl-Cr(Mo) composite containing Hf was directionally solidified under Ar atmosphere in Al2O3-SiO2 ceramic mold by the standard Bridgman method. The microstructure in the as-grown and hot isostatic pressing (HIP) conditions was studied using SEM, HREM and TEM equipped with EDXS. The composite was mainly composed of three phases, i.e. lamellar Cr(Mo), NiAl matrix and semi-continuously distributed Ni2AlHf. The common growth direction of NiAl and Cr(Mo) is < 111 >, and the interface between them was atomically flat with no transition layer. Fine G-phase precipitates were formed in the presence of Si which was from the ceramic shell molds used during the directional solidification. The G-phase precipitates were cuboidal in shape and coherent with NiAl matrix. After the HIPed and aged treatment, the G-phase precipitates completely disappeared and the amount of intercellular Ni2AlHf phase was partially reduced. The mechanical properties were measured by tensile and compressive tests within the temperature range of 25 similar to 1100 degreesC. The BDTT of the HIPed and aged materials is significantly higher than the as-grown composite. The yield stress of the composite was higher than that of many NiAl-based alloys and possible strengthening mechanism were discussed. (C) 2001 Elsevier Science Ltd. All rights reserved.
WOS研究方向	Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering
语种	英语
出版者	ELSEVIER SCI LTD
WOS记录号	WOS:000168566700004
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/111850]
专题	金属研究所_中国科学院金属研究所
通讯作者	Guo, JT
作者单位	Chinese Acad Sci, Met Res Inst, Shenyang 110016, Peoples R China
推荐引用方式 GB/T 7714	Guo, JT,Cui, CY,Chen, YX,et al. Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite[J]. INTERMETALLICS,2001,9(4):287-297.
APA	Guo, JT,Cui, CY,Chen, YX,Li, DX,&Ye, HQ.(2001).Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite.INTERMETALLICS,9(4),287-297.
MLA	Guo, JT,et al."Microstructure, interface and mechanical property of the DS NiAl/Cr(Mo,Hf) composite".INTERMETALLICS 9.4(2001):287-297.