Short-term oxidation resistance and degradation of Cr2AlC coating on M38G superalloy at 900-1100 degrees C | |
Li, J. J.1,2; Li, M. S.1; Xiang, H. M.1,2; Lu, X. P.1,2; Zhou, Y. C.1 | |
刊名 | CORROSION SCIENCE |
2011-11-01 | |
卷号 | 53期号:11页码:3813-3820 |
关键词 | Ceramic Sputtered films Oxidation Internal oxidation |
ISSN号 | 0010-938X |
DOI | 10.1016/j.corsci.2011.07.032 |
通讯作者 | Li, M. S.(mshli@imr.ac.cn) |
英文摘要 | High temperature oxidation behavior of the Cr2AlC coating was investigated at 900-1100 degrees C. During the oxidation, a continuous Al2O3 scale formed, resulting in the improvement of the oxidation resistance of the substrate. Meanwhile, the oxidation induced depletion of Al within the Cr2AlC coating resulted in the transformation of Cr2AlC to Cr-C phases. Compared with bulk Cr2AlC, the Cr2AlC coating possessed similar oxidation behavior, but with higher oxidation rate. This is because a great number of columnar grain boundaries existed in the as-deposited coating, through which oxygen and nitrogen could diffuse inwardly, resulting in the internal oxidation and nitridation. (C) 2011 Elsevier Ltd. All rights reserved. |
资助项目 | National Science Foundation of China[50771099] ; National Science Foundation of China[50832008] |
WOS研究方向 | Materials Science ; Metallurgy & Metallurgical Engineering |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
WOS记录号 | WOS:000295434500041 |
资助机构 | National Science Foundation of China |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/105016] |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Li, M. S. |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Li, J. J.,Li, M. S.,Xiang, H. M.,et al. Short-term oxidation resistance and degradation of Cr2AlC coating on M38G superalloy at 900-1100 degrees C[J]. CORROSION SCIENCE,2011,53(11):3813-3820. |
APA | Li, J. J.,Li, M. S.,Xiang, H. M.,Lu, X. P.,&Zhou, Y. C..(2011).Short-term oxidation resistance and degradation of Cr2AlC coating on M38G superalloy at 900-1100 degrees C.CORROSION SCIENCE,53(11),3813-3820. |
MLA | Li, J. J.,et al."Short-term oxidation resistance and degradation of Cr2AlC coating on M38G superalloy at 900-1100 degrees C".CORROSION SCIENCE 53.11(2011):3813-3820. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论