Elevated temperature mechanical properties of a directionally solidified NiAl/Cr(Mo)-Hf alloy | |
Xu, CM; Guo, JT; Xie, XS | |
刊名 | ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4
![]() |
2005 | |
卷号 | 297-300页码:1477-1481 |
关键词 | NiAl/Cr(Mo)-Hf alloy microstructure brittle-to-ductile transition temperature (BDTT) fracture morphology |
ISSN号 | 1013-9826 |
通讯作者 | Xu, CM(cmxu@imr.ac.cn) |
英文摘要 | The microstructure of directionally solidified (DS) NiAl-28Cr-5Mo-1Hf eutectic alloy was investigated by SEM and TEM. The eutectic alloy is composed of NiAl matrix, Cr (Mo) phase and a small amount of Heusler phase. Tensile testing of this alloy was performed from room temperature to 1373K. The brittle-to-ductile transition temperature (BDTT) is dependent on strain rate, with two orders of increase on strain rate resulting in a 100K increase in transition temperature. The observation of fracture surface showed that at temperature above BDTT, the fractograph changes from NiAl cleavage and debonding along NiAl/Cr(Mo) interface boundary to ductile in nature. |
WOS研究方向 | Materials Science ; Mechanics |
语种 | 英语 |
出版者 | TRANS TECH PUBLICATIONS LTD |
WOS记录号 | WOS:000233131202007 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/83882] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
通讯作者 | Xu, CM |
作者单位 | 1.Chinese Acad Sci, Inst Met Res, Shenyang, Peoples R China 2.Beijing Univ Sci & Technol, Beijing 100083, Peoples R China |
推荐引用方式 GB/T 7714 | Xu, CM,Guo, JT,Xie, XS. Elevated temperature mechanical properties of a directionally solidified NiAl/Cr(Mo)-Hf alloy[J]. ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4,2005,297-300:1477-1481. |
APA | Xu, CM,Guo, JT,&Xie, XS.(2005).Elevated temperature mechanical properties of a directionally solidified NiAl/Cr(Mo)-Hf alloy.ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4,297-300,1477-1481. |
MLA | Xu, CM,et al."Elevated temperature mechanical properties of a directionally solidified NiAl/Cr(Mo)-Hf alloy".ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4 297-300(2005):1477-1481. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论