Microstructures and Properties of Porous Liquid-Phase-Sintered SiC Ceramic by Hot Press Sintering | |
Li, Yajie; Wu, Haibo; Liu, Xuejian; Huang, Zhengren | |
刊名 | MATERIALS
![]() |
2019-02-02 | |
卷号 | 12期号:4 |
关键词 | silicon carbide liquid phase sintering porosity microstructure strength |
ISSN号 | 1996-1944 |
DOI | 10.3390/ma12040639 |
文献子类 | Article |
英文摘要 | Porous liquid-phase-sintered SiC (L-SiC) ceramics were successfully fabricated by hot press sintering (HP) at 1800 degrees C in argon, using Al2O3 and Y2O3 as oxide additions. By varying the starting coarse SiC particle size, the relationships between pore microstructures and flexural strength as well as gas permeability of porous L-SiC were examined. All the as-sintered samples possessed homogeneous interconnected pores. The porosity of porous L-SiC decreased from 34.0% to 25.9%, and the peak pore size increased from 1.1 to 3.8 m as the coarse SiC particle sizes increased. The flexural strengths of porous L-SiC ceramics at room temperature and 1000 degrees C were as high as 104.3 +/- 7.3 MPa and 78.8 +/- 5.1 MPa, respectively, though there was a decrease in accordance with their increasing pore sizes and particle sizes. Moreover, their gas permeability increased from 1.4 x 10(-14) m(2) to 4.6 x 10(-14) m(2) with the increase of pore size in spite of their decreased porosity. |
WOS研究方向 | Materials Science |
语种 | 英语 |
出版者 | MDPI |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/27345] ![]() |
专题 | 中国科学院上海硅酸盐研究所 |
推荐引用方式 GB/T 7714 | Li, Yajie,Wu, Haibo,Liu, Xuejian,et al. Microstructures and Properties of Porous Liquid-Phase-Sintered SiC Ceramic by Hot Press Sintering[J]. MATERIALS,2019,12(4). |
APA | Li, Yajie,Wu, Haibo,Liu, Xuejian,&Huang, Zhengren.(2019).Microstructures and Properties of Porous Liquid-Phase-Sintered SiC Ceramic by Hot Press Sintering.MATERIALS,12(4). |
MLA | Li, Yajie,et al."Microstructures and Properties of Porous Liquid-Phase-Sintered SiC Ceramic by Hot Press Sintering".MATERIALS 12.4(2019). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论