Corrosion-driven outward migration and growth of helium bubbles in a nickel-based alloy in high-temperature molten salt environment | |
Lei, GH; Yang, SD; Huang, HF; Huang, Q; Liu, RD; Zhang, W; Yu, GJ; Yan, L | |
刊名 | CORROSION SCIENCE |
2019 | |
卷号 | 153期号:-页码:47—52 |
关键词 | STRUCTURAL-MATERIALS GAS-RELEASE IRRADIATION NI PERFORMANCE CHALLENGES ELEMENTS CRACKING SURFACE METALS |
ISSN号 | 0010-938X |
DOI | 10.1016/j.corsci.2019.03.026 |
文献子类 | 期刊论文 |
英文摘要 | High-temperature helium ion irradiation was conducted on a nickel-based alloy at 650 degrees C. A unique outward migration of helium bubbles was observed in the irradiated alloy under molten salt environment, distinguished from the evolution of helium bubbles induced by room-temperature irradiation, which is related to the deficit of vacancies in the high-temperature irradiated alloy and slow growth rate of the bubbles. Moreover, it was elucidated that corrosion induced vacancies rather than high-temperature annealing effect of molten salt is responsible for the evolution of helium bubbles formed by high-temperature helium ion irradiation. |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/31533] |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
作者单位 | 1.Shanghai Spaceflight Precis Machinery Inst, Shanghai 201600, Peoples R China 2.Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China; 3.Univ Chinese Acad Sci, Beijing 100049, Peoples R China; |
推荐引用方式 GB/T 7714 | Lei, GH,Yang, SD,Huang, HF,et al. Corrosion-driven outward migration and growth of helium bubbles in a nickel-based alloy in high-temperature molten salt environment[J]. CORROSION SCIENCE,2019,153(-):47—52. |
APA | Lei, GH.,Yang, SD.,Huang, HF.,Huang, Q.,Liu, RD.,...&Yan, L.(2019).Corrosion-driven outward migration and growth of helium bubbles in a nickel-based alloy in high-temperature molten salt environment.CORROSION SCIENCE,153(-),47—52. |
MLA | Lei, GH,et al."Corrosion-driven outward migration and growth of helium bubbles in a nickel-based alloy in high-temperature molten salt environment".CORROSION SCIENCE 153.-(2019):47—52. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论