Formation of chromium carbide coatings on HT250 steel by thermal diffusion processes in fluoride molten salt bath | |
Su, XZ; Zhao, SF; Hou, J; Yu, GJ; Chen, YJ; Sun, H; Zhang, P; Xie, LD | |
刊名 | VACUUM |
2018 | |
卷号 | 155期号:-页码:219-223 |
关键词 | REACTIVE DEPOSITION MECHANICAL-PROPERTIES GROWTH-BEHAVIOR FLINAK SALT MICROSTRUCTURE KINETICS ELECTRODEPOSITION TEMPERATURE SUBSTRATE FRICTION |
ISSN号 | 0042-207X |
DOI | 10.1016/j.vacuum.2018.06.015 |
文献子类 | 期刊论文 |
英文摘要 | LiF-NaF-KF (46.5-11.5-42 mol %, FLiNaK) molten salt was used in the thermal diffusion (TD) process to form chromium carbide coatings on gray cast iron HT250 at 900 degrees C for 8 h. The structure and chemical composition of the coating were observed by scanning electron microscopy coupled with energy dispersive X-ray microanalysis (SEM-EDX) and X-ray diffraction (XRD). Both the nanoindentation hardness and Vickers hardness were measured. A 3-5 mu m thick chromium carbides layer and approximately 10 pm thick transition layer were formed on the surface of gray cast iron HT250. The chromium carbides layer was composed of Cr23C6 and Cr7C3. The hardness of gray cast iron HT250 was increased 6 times after treatment. The tribological behavior was also improved. These results demonstrate that fluoride salts can be used as base salts to form excellent chromium carbides coatings via the TD process. |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/30951] |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
作者单位 | 1.Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Su, XZ,Zhao, SF,Hou, J,et al. Formation of chromium carbide coatings on HT250 steel by thermal diffusion processes in fluoride molten salt bath[J]. VACUUM,2018,155(-):219-223. |
APA | Su, XZ.,Zhao, SF.,Hou, J.,Yu, GJ.,Chen, YJ.,...&Xie, LD.(2018).Formation of chromium carbide coatings on HT250 steel by thermal diffusion processes in fluoride molten salt bath.VACUUM,155(-),219-223. |
MLA | Su, XZ,et al."Formation of chromium carbide coatings on HT250 steel by thermal diffusion processes in fluoride molten salt bath".VACUUM 155.-(2018):219-223. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论