Undercooling and Rapid Solidification of Nb-Si Eutectic Alloys Studied by Long Drop Tube | |
Wang YR(王育人); Dong SY; Wei BC(魏炳忱); Li WH(李维火) | |
2005-10-09 | |
会议名称 | 6th International Workshop on Advanced Intermetallic and Metallic Materials, OCT 09-15, 2005, Yangzhou, PEOPLES R CHINA |
通讯作者 | 王育人 |
中文摘要 | Niobium-silicide alloys have great potential for high temperature turbine applications. The two-phase Nb/Nb5Si3 in situ composites exhibit a good balance in mechanical properties. Using the 52 in drop tube, the effect of undercooling and rapid solidification on the solidification process and micro-structural characterization of Nb-Si eutectic alloy was studied. The microstructures of the Nb-Si composites were investigated by optics microscope (OM), X-ray diffraction (XRD) and scanning electron microscope (SEM) equipped with X-ray energy dispersive spectrometry (EDS). Up to 480 K, deep undercooling of the Nb-Si eutectic samples was successfully obtained, which corresponds to 25% of the liquidus temperature. Contrasting to the conventional microstructure usually found in the Nb-Si eutectic alloy, the microstructure of the undercooled sample is divided into the fine and coarse regions. The most commonly observed microstructure is Nb+Nb5Si3, and the Nb3Si phase is not be found. The change of coarseness of microstructure is due to different cooling rates during and after recalescence. The large undercooling is sufficient to completely bypass the high temperature phase field. |
收录类别 | CPCI-S |
会议录 | TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2006,16(suppl.2):S89-S92 |
学科主题 | 力学 |
语种 | 英语 |
ISSN号 | 1003-6326 |
WOS记录号 | WOS:000241774000019 |
内容类型 | 会议论文 |
源URL | [http://dspace.imech.ac.cn/handle/311007/13763] |
专题 | 力学研究所_力学所知识产出(1956-2008) |
推荐引用方式 GB/T 7714 | Wang YR,Dong SY,Wei BC,et al. Undercooling and Rapid Solidification of Nb-Si Eutectic Alloys Studied by Long Drop Tube[C]. 见:6th International Workshop on Advanced Intermetallic and Metallic Materials, OCT 09-15, 2005, Yangzhou, PEOPLES R CHINA. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论