Thermal Shock Resistance of APS 8YSZ Thermal Barrier Coatings on Titanium Alloy | |
Zeng SB ; Liu YJ ; Fan XZ ; Huang WZ ; Gu LJ ; Zou BL ; Chen XL ; Khan ZS ; Zhu L ; Yang DW ; Cao XQ | |
刊名 | journal of thermal spray technology |
2012 | |
卷号 | 21期号:2页码:335-343 |
关键词 | OXIDATION BEHAVIOR THERMOPHYSICAL PROPERTIES FAILURE MECHANISMS HIGH-TEMPERATURE TI-6AL-4V ALLOY AL COATINGS GROWN OXIDE DIFFUSION PROTECTION NI |
ISSN号 | 1059-9630 |
通讯作者 | cao xq |
中文摘要 | thermal barrier coatings (tbcs) with a typical 8ysz ceramic top coat and conicraly bond coat were deposited on titanium alloy substrate (ti-6al-4v in wt.%) by air plasma spraying. thermal insulation and thermal shock resistance of the tbcs at different temperatures as well as their failure behavior were investigated. the results showed that the test temperature had a significant effect on thermal shock life of the tbcs. failure of the tbcs systems was caused by the formation of crack, bond coat oxidation and elemental diffusion. the vertical cracks induced by thermal shock cycles were probably responsible for the enhancement in thermal shock resistance of the tbcs. furthermore, elemental diffusion had a great effect on the acceleration of the tbcs failure. the tbcs could provide a good thermal protection for the titanium alloy substrate. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000303472600013 |
公开日期 | 2013-06-08 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/48283] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Zeng SB,Liu YJ,Fan XZ,et al. Thermal Shock Resistance of APS 8YSZ Thermal Barrier Coatings on Titanium Alloy[J]. journal of thermal spray technology,2012,21(2):335-343. |
APA | Zeng SB.,Liu YJ.,Fan XZ.,Huang WZ.,Gu LJ.,...&Cao XQ.(2012).Thermal Shock Resistance of APS 8YSZ Thermal Barrier Coatings on Titanium Alloy.journal of thermal spray technology,21(2),335-343. |
MLA | Zeng SB,et al."Thermal Shock Resistance of APS 8YSZ Thermal Barrier Coatings on Titanium Alloy".journal of thermal spray technology 21.2(2012):335-343. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论